The solvent-based fire retardant coating based on acrylic resin with special pigment and additives, which will be inflated with the fire or heat to form a fine foam layer. This foam layer can insulate substrates to contact with the fire, therefore consumedly cut down flammability of flammable substrates and retard the transmission of heat and the expansion of fire.

1. Very fast drying.

2. Inflated above several times when occurred the fire to    rapidly reach the fireproof and fire-retardant effects.

3. Carbonized foam body can resist high temperature up to 1000℃

White or desired colors

1.40 ± 0.05 Kg/L

Flat

Set-to-touch1 hr.  Dry hard 3 hrs.   (25 ℃)

Min.   2 hrs.

1. CNS 6532 class 3 :   min. 3 times

2. ASTM E84 class A :   min. 2 times

2. ASTM E84 class A :   D.F.T.   above   150   microns

1. CNS 6532 class 3:    727 g/ meter square                                       (7.2 meter square   /Gal)

2. ASTM E84 class A: 150 ft2/Gal   (13.9 meter square /Gal)

1.Before application, stir paint evenly, when paint is too thick, polyurethane thinner within specified quantity can be added.

2. Adhered moisture, grease, rust, dirt or loose paints film on substrate must be cleaned thoroughly.

3.Rough the smooth surface with sand papers and avoid applying the paint in humid exceed 85% RH or temperature low to 5℃.

4. The fireproof effect and dry film thickness of fire retardant coating is in direct proportion, namely the dry film thickness is more thick and the intumescent effect of paint film is better, the fireproof effect is better too.