EPOXY SPLASH ZONE CLADING (SPRAY)

PRODUCT NUMBER

1085SP

TYPE

A two-pack, it based on epoxy resin with supreme anti corrosion ability.

USES

Used for the splash zone of coast and harbor facilities, or for the steel and concrete of the underwater area.

CHARACTERISTICS

1.Easy applying in water with good adhesion.

2.Excellent ability permeates the humid surface of steel and cement to inhibit corrosion.

3.Excellent water resistance, especially to anti cathode corrosion. 

4.Excellent chemical resistances..

5.Excellent resistance to abrasion and hitting.

6.1500 paint film with one coat

FINISH

Semi-gloss

COLOR

Desired colors

MASS DENSITY

Above 1.4Kg/L (mixture)

FLASH POINT

Above 25℃

VISCOSITY(25℃)

Above 120KU (mixture)

DRYING TIME

Set-to-touch: 2 hr.    Dry hard: 8 hrs.     Fully cured: 7days (25℃)

OPTIMUM FILM THICKNESS

Wet  1660μ           Dry: 1550μ

OVERCOATING INTERVALS

Min.  12 hrs.           Max. 7 days  

MIXING RATIO

Base: hardener = 86.7 : 13.3  (by wt.)

VOLUME SOLIDS

Above 90%

THEORETICAL COVERAGE

0.6m²/ L   0.43m²/KG

THINNER

No.1005 Epoxy Thinner (SP-12)  (Only for cleaning tools)

PRECEDING COATS

SUBSEQUENT COAT

No.700    One pack polyurethane maintenance primer

No.1073   Epoxy clear cement primer

Epoxy top coat, Polyurethane top coat

POT LIFE

1.5 hours (mixture, 25℃)

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

APPLICATION METHOD

FOR AIRLESS SPRAY

Airless, trowel, Brush

Tip size      0.035”~0.045”

Air pressure  5~6Kg/cm²

Pump ration  60:1 or greater

NOTE

1.All equipment must be cleaned after using.

2.Base and Initiator need to be well stirred and blended

3.Please notice adequate ventilation must be provided when working in tanks