PRODUCT NUMBER

FIRECUT FM-906

TYPE

The water-based intumescent paint based on nonflammable resin with special pigment and additives also has a fire protection efficacy. The paint film will be to form a foam layer like sponge when occurred to the fire. This foam layer is a good hot-block to reduce the temperature rising speed of steel structures.

USES

Used for beams and columns of steel structures and the fire protection performance.

CHARACTERISTICS

1.Low reactive temperature:When temperature was reached to 200℃ above, the paint film may form a foam layer with the increasing room temperature to rapidly expand hot-block for several times to protect structures safely.

2.No asbestos ingredient:Contents did not have asbestos fiber.

3.Thin paint film:Excellent fire protection in only thin paint film then can reach the fire protection.

4.Smooth and good appearance:The finish has good smooth film also may top various color paints.

5.Be able to high-build and easy apply.

FINISH

Flat

COLOR

White

SPECIFIC GRAVITY

1.30 ± 0.1 Kg/L (25℃)

FLASH POINT

Above 100℃

DRYING TIME(25℃)

Set-to-touch 0.5 hr

OVERCOATING INTERVALS

Spary:min. 4 hrs.        Brush: min. 1 hr.

SOLIDS CONTENT

NV:69% ± 3%

PRECEDING COATS

No.1076 Epoxy Zinc Phosphate Primer(EP-66)

SUBSEQUENT COATS

Water-based topcoats(No.406 FM)

THEORETICAL COVERAGE

The weight of unit area, wet film thickness and dry film thickness for per coat to refer as follows:

STANDARD OF FIRE TEST

BS 476 Part 21 Methods for determination of the fire resistance of loadbearing elements of construction.

STORAGE SHELF LIFE

Minimum 12 months under normal storage conditions

APPLICATION METHOD

Airless Spary, or Brush

FOR AIRLESS SPRAY

Tip Size:0.023”~0.027”

Air Pressure:50~80 psi

Pump Ratio: 45:1 or greater

NOTE

1. Maximum 2 times by spray or 4 times by brush within 24 hours.

2. Adhered moisture, grease, rust, dirt or loose paints film on substrate must be cleaned thoroughly.

3. Avoid applying the paint in temperature low to 5℃ or humid exceed 85% RH , particularly, the wet surface must be thoroughly dried.

4. The fire resistance mastic coating can not be drenched with rain directly before applying the topcoat.