EPOXY HIGH SOLIDS GLASS FLAKE COATING

PRODUCT NUMBER

1061GF (EP-999GF)

TYPE

The high solids glass flake paint based on epoxy resin with anticorrosive pigment.

USES

Used for ship, bridges, storage tanks, pipelines, petrochemical plants and steel structures.

CHARACTERISTICS

1. Tough and hard film, excellent abrasion resistance.

2. Excellent corrosion and water resistance.

3. Green anticorrosion pigment formula, excellent inhibitory type and hiding type anticorrosion performance for the steel.

4. Excellent resistance to oils and chemicals.

5. Can be coated in or can be coated with a variety of coatings, is the best maintenance paint.

6. Suitable for loading grain.

7. Excellent corrosion resistance, when collocate with PU700 primer and high weather resistant topcoat, the anti-corrosion performance is especially outstanding.

COLOR

Brown, Gray

FLASH POINT

Above 25℃

MASS DENSITY

Above 1.4 Kg/L ( mixture)

DRYING TIME

Set-to-touch   4 hrs.      Dry hard   12 hrs.      Fully cured   7days (25℃)

OPTIMUM FILM THICKNESS

Wet    188 microns       Dry   150 microns

VOLUME SOLIDS

Above 75%

THEORETICAL COVERAGE

20.0 m² /Gal      5.3 m² /L      3.8 m² /Kg

OVERCOATING INTERVALS

Min. 6 hrs. (25℃)

THINNER

SP-12 Epoxy Thinner (5~25%).

PRECEDING COATS

No.1006 Epoxy Zinc Rich Primer   

No.1011 Inorganic Zinc Rich Primer

No.700 One Pack Polyurethane Maintenance Primer

No.1020 Epoxy Alloy Primer    

No.1075 Epoxy Aluminum Tripolyphosphate Primer

SUBSEQUENT COATS

Epoxy, Polyurethane or Fluorocarbon resin system

MIXING RATIO

Base : Hardener = 83 : 17 ( by wt. )

POT LIFE

4 hrs.  ( mixture, 25℃)

STORAGE SHELF LIFE

Minimum 2 years under normal storage conditions.

APPLICATION METHOD

Airless spray, Brush, Roller

FOR AIRLESS SPRAY

Tip size      0.025”~ 0.029”          Air pressure  5~6 Kg/cm²

Pump ratio   45 : 1 or greater