White and black POM sheet manufacturer
USD $4 - $8 /Piece
Min.Order:500 Pieces
Ningjin Jutai Chemical & Plastic Co., Ltd.
POM Description
Good mechanical properties and rigidity, and close to the metal material. It’s an ideal replacement material of copper, cast zinc, steel, aluminum and other metal materials. Excellent fatigue resistance and creep resistance. Good abrasion resistance, self-lubricated and friction. High thermal stability, good chemical stability and excellent electrical insulation. And it can be used in temperatures ranging from -50°C to +110°C.
POM Characteristics
High surface hardness, low abrasion consumption, impact fatigue and shock resistance, low coefficient friction, and self- lubricating, therefore, it is the first material choice for manufacturing gear.
High mechanical strength and rigidity. Although the contraction rate is high, the dimension is stable.
Good dielectric properties, solvent resistance, non-stress cracking, no porosity.
Torsional resistance, it can be restored to the original shape when removing the external force.
Low water absorption
POM Applications
Machinery industry used to produce gears, springs, bearings, wheels, connecting rod, impeller blades etc..
Automobile industry
Electronic and electrical appliances
Others such as toys, windows, water tanks and washing basins
Specifications:
1).Thickness: 0.5-90mm
2).General Size: 600mm×1200mm 600mm×1000mm 1000mm×2000mm 1000mm*1200mm
3).white, black, red green ect.
POM performance
Property | unit | copolymerization | homopolymer |
|
Density | g/cm3 | 1.425 | 1.41 |
|
Moisture | % | 0.25 | 0.22 |
|
Tensile | MPa | 68.6 | 60.37 |
|
Elongation ratio | % |
|
|
|
Bending strength | MPa | 96.04 | 89.18 |
|
Compression strength | Mpa | 123.48 | 109.76 |
|
Impact | KJ/m | 7.6 | 12.5 |
|
Hardness | RH | (M94,R120) | (M78-80) |
|
Specific heat volume | J/Kg.k | / | / |
|
Temperaure of thermal deformation °C 0.45MPa | °C | 170 | 158 |
|
Volume resistivity | Ω.m | 6x1014 | 1x1014 |
|
Dielectric Strength(3.2mmThickness) | Kv/mm | 18.6 | 19.7 |
|
Resistant arc characteristic | S | 240 |
| |
Sunlight influence | slight white |
| ||
Strong-acid influence | corrode |
| ||
Alkali influence | some resistance |
| ||
Organic solvent | fine |
|