Specifications

POM rod
1. Non-Toxic and smell
2. Low coefficient of friction
3.wear resistance
4.high crystalline

 

 

 

Description of POM  

 

POM is a smooth, shiny, hard and dense material. Its color is yellow or white, the thin-walled part is translucent. It is easy to burn from the fire and continued to burn when left the fire. The top of the 

flame is yellow,  and bottom is blue,there’s melt dripping, and a strong irritant smell of formaldehyde, like fish 

stench. POM is a white powder, generally not transparent, stainability, the density is 1.41-1.43 g / cm3, the molding shrinkage is 1.2-3.0% , molding temperature is 170-200 °C, drying conditions is 

80-90 °C and 2 hours. POM long-term heat resistance is not high, but it can reach up to 160 °C in short term. It can be used for a long time under the temperature of -40 °C -100 °C temperature range. POM is easily decomposed and its decomposed temperature is 240 degrees. 

Decomposition will generate irritating and corrosive gas.So the mold needs to be made by corrosion resistance 

materials.

 

 

Application of POM rod:

 

• Machinery industry used to produce gears, springs, bearings, wheels, connecting rod, impeller blades etc..
• Automobile industry
• Electronic and electrical appliances
• Others such as toys, windows, water tanks and washing basins 

 

 

POM performance

 

Property	unit	copolymerization	homopolymer
Density	g/cm3	1.425	1.41
Moisture	%	0.25	0.22
Tensile	MPa	68.6	60.37
Elongation ratio	%
Bending strength	MPa	96.04	89.18
Compression strength	Mpa	123.48	109.76
Impact	KJ/m	7.6	12.5
Hardness	RH	(M94,R120)	(M78-80)
Specific heat volume	J/Kg.k	/	/
Temperaure of thermal deformation °C 0.45MPa	°C	170	158
Volume resistivity (wetness50%23°C)	Ω.m	6x1014	1x1014
Dielectric Strength(3.2mmThickness)	Kv/mm	18.6	19.7
Resistant arc characteristic	S	240
Sunlight influence	slight white
Strong-acid influence	corrode
Alkali influence	some resistance
Organic solvent	fine