Specifications

POM sheet
1. Non-Toxic and smell
2. Low coefficient of friction
3.wear resistance
4.high crystalline

 

 

Description of POM sheet

 

POM has characteristics of rigid, high stiffness, good flexibility, antifriction and wear resistance. It has excellent mechanical properties, specific strength is up to 50.5MPa, specific 

stiffness is up to 2650MPa which is very close to metal. The mechanical properties of POM changes small with 

temperature, copolymer POM changes slightly larger than homopolymer POM. POM has high impact strength, 

but the conventional impact is less than  ABS and PC, POM for notch sensitivity, The notches ones impact 

strength can drop as much as 90%. POM fatigue strength is very prominent, its fatigue strength can reach 

35MPaafter 10 alternating loads up, while the PA and PC is only 28MPa. Creep resistance of POM and PA  is 

similar, under the situation of 20 C, 21MPa, 3000h its only get 2.3%, and it is little affected by temperature. POM friction factor is small, about wear

 resistance, POM> PA66> PA6> ABS> HPVC> PS> PC, its PV limit is very large, and it can be self-lubricated.

 

Specifications: 

 

1).Thickness: 0.5-90mm

 

2).General Size: 600mm×1200mm 600mm×1000mm 1000mm×2000mm  1000mm*1200mm

 

 

Color:

 

white, black, red green ect.

 

 

Application:  

 

 

1.Machinery industry used to produce gears, springs, bearings, wheels, connecting rod, impeller blades etc..

2.Automobile industry

3.Electronic and electrical appliances

4.Others such as toys, windows, water tanks and washing basins 

 

POM performance

 

Property	unit	copolymerization	homopolymer
Density	g/cm3	1.425	1.41
Moisture	%	0.25	0.22
Tensile	MPa	68.6	60.37
Elongation ratio	%
Bending strength	MPa	96.04	89.18
Compression strength	Mpa	123.48	109.76
Impact	KJ/m	7.6	12.5
Hardness	RH	(M94,R120)	(M78-80)
Specific heat volume	J/Kg.k	/	/
Temperaure of thermal deformation °C 0.45MPa	°C	170	158
Volume resistivity (wetness50%23°C)	Ω.m	6x1014	1x1014
Dielectric Strength(3.2mmThickness)	Kv/mm	18.6	19.7
Resistant arc characteristic	S	240
Sunlight influence	slight white
Strong-acid influence	corrode
Alkali influence	some resistance
Organic solvent	fine