ASTM A335 P92 is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
Each length of pipe shall be subjected to the hydrostatic test. Also, each pipe shall be examined by a non-destructive examination method in accordance to the required practices. The range of ASTM A335 P92 seamless alloy steel pipe sizes that may be examined by each method shall be subjected to the limitations in the scope of the respective practice.
The different mechanical test requirements for pipes, namely, transverse or longitudinal tension test, flattening test, and hardness or bend test are presented.Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
Chemical Requirements of ASTM A335 P92
UNS Designation | K92460 |
Carbon | 0.07–0.13 |
Manganese | 0.30–0.60 |
Phosphorus(max) | 0.02 |
Sulfur(max) | 0.01 |
Silicon | 0.50 max |
Chromium | 8.50–9.50 |
Molybdenum | 0.30–0.60 |
V | 0.15-0.25 |
N | 0.03-0.07 |
Ni (max) | 0.4 |
Al(max) | 0.02 |
Cb | 0.04-0.09 |
W | 1.5-2.00 |
B | 0.001-0.006 |
Ti (max) | 0.01 |
Zr(max) | 0.01 |
Mechanical Properties of ASTM A335 P92
Tensile strength, min, (MPa) | 620 |
Yield strength, min, (MPa) | 440 |
Elongation, min, (%), L/T | 20/… |
Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
Mechanical Tests Specified of ASTM A335 P92
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
ProtectionBlack and Bare: External Varnished with Black or Clear LAcquer
Mill test certificate: MTC is issued in accordance with EN 10204.
Astm A335 standard specication for seamless ferritic alloy-steel pipe for high-temperature service
ASTM A335 standard is issued under the fixed designation A 335/A 335M; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision.
Astm A335 standard specication for seamless ferritic alloy-steel pipe
This specification covers nominal (average) wall seamless alloy-steel pipe intended for high-temperature service (Mote 1). Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Selection will depend upon design, service conditions, mechanical properties, and high-temperature characteristics.