Specifications

1) fine and uniformity cells
2) low thermal conductivity
3) perfect fire resistance

Product Introduction

RIGID POLYURETHANE BLEND POLYOLS FOAM SYSTEM FOR SPRAY INSULATION

DQT-501B is high density spray blend polyols, it reacts with isocyanate to produce foam which has excellent performances as below,

    1) fine and uniformity cells

    2) low thermal conductivity

    3) perfect fire resistance

    4)excellent low temperature dimentional stability .

 

It applies to all kinds of thermal insulation engineering which use the spray, such as cold warehouses, pots, large-scale pipelines, construction roofs and all types of abnormal thermal insulation projects.

 

Physical Properties

Appearance                   Hydroxyl Value                mgKOH/g Dynamic Viscosity (25 °C)       mpa.s Gravity (20 °C )                g/ml Storage Temperature             °C Storage Stability               month

Light yellow to brown viscous liquid 200-300 100-200 1.12-1.20 10-25 6

 

Recommended Ratio

	pbw
DQT-501B blend polyols Isocyanate	100 100-105

 

Reactivity Characteristics

Component temperature is 20°C, the actual value is varied according to pipe diameter and processing condition.  

RT                         s GT                         s

3-5 6-12

 

Foam Performances

Items	Test Method	Index
Spray Density                  Closed-cell Rate            Initial Thermal Conductivity(15°C)        Compressive Strength Adhesive Strength  Elongation at break Dimensional Stability  24h  -20°C  24h   70°C  Water Absorption                      Oxygen Index	GB 6343 GB 10799 GB 3399 GB/T8813 GB/T16777 GB/T9641 GB/T8811   GB 8810 GB 8624	≥50kg/m3 ≥90% ≤24mW/(m.K) ≥300kPa ≥120kPa ≥10% ≤1% ≤1.5% ≤3% ≥26

The data provided above are typical value, which are tested by our company. For our company's products, the data included in the law do not have any constraints.