Specifications

Blend polyether polyols, HCFC-141B foaming agent, used for spray insulation

DQT-501A is spray blend polyether polyols, it reacts with isocyanate to produce foam has excellent performances, which are as follows,

 

1.fine and uniformity cells

2.low thermal conductivity

3.perfect fire resistance

4.excellent low temperature dimentional stability

 

It applies to all kinds of thermal insulation projects use the spray, such as storage room, large pots, large-scale pipelines and construction our-wall or inner-wall etc. 

 

This is our second factory we use our own polyurethane.

 

Physical Properties

Appearance                       pale yellow transparent viscous liquid

Hydroxyl Value mgKOH/g                            200-300 

Dynamic Viscosity (25 °C) mPa.s             100-200

Gravity (20 °C ) g/ml                                     1.12-1.20

Storage Temperature °C                               10-25

Storage Stability month                                       6

Recommended Ratio                                pbw 
DQT-501A                                                          100

Isocyanate                                                       100-105

 

Reactivity characteristics  (the exact value varied depending on processing conditions)

Cream time s                                                     3-5

Gel time s                                                           6-10

 

 

Foam Performance

Spray density                                          GB 6343               35 kg/m3  

Closed-cell rate                                     GB 10799             ≥90%           

Initial thermal conductivity (15°C)       GB3399                24mW/(m.k)

Compressive strength                          GB/T8813             ≥ 150 Mpa     

Adhesive strength                                  GB/T 16777         ≥ 120 Mpa

Elongation at break                                GB/T9641             ≥ 10%

Dimentional stability  24h -20°C           GB/T8811             ≤1 %

                                        24h  70°C                                        ≤1.5%

Water absorption                                     GB 8810              ≤3%

Oxygen index                                             GB 8624              ≥26