Specifications

DQT-501C is spray blend polyols, foaming agent is HFC-365mfc/HFC-245fa instead of HCFC-141B, it reacts with isocyanate to produce foam which has excellent performances as follows,

1.fine and uniformity cells

2.low thermal conductivity

3.perfect fire resistance

4.excellent low temperature dimentional stability

It applies to all kinds of thermal insulation engineering which use the spray, such as storage warehouse, large pots, large-scale pipelines and construction roof and all types of abnormal thermal insulation projects. 

This is our second factory we use our own polyurethane to built it.

Physical Properties

Appearance                       pale yellow transparent viscous liquid

Hydroxyl Value mgKOH/g                            200-300 

Dynamic Viscosity (25 °C) mPa.s             100-200

Gravity (20 °C ) g/ml                                     1.12-1.20

Storage Temperature °C                              10-25

Storage Stability month                                    6

Recommended Ratio                          pbw 
DQT-501A                                                        100

Isocyanate                                                    100-105

Reactivity characteristics   (the exact value varied depending on processing conditions)

Cream time s                                                  3-5

Gel time s                                                       6-10

Foam Performance

Spray density                                         GB 6343               35 kg/m3  

Closed-cell rate                                    GB 10799             ≥90%           

Initial thermal conductivity (15°C)      GB3399                24mW/(m.k)

Compressive strength                         GB/T8813            ≥ 150 Mpa     

Adhesive strength                                 GB/T 16777         ≥ 120 Mpa

Elongation at break                              GB/T9641             ≥ 10%

Dimentional stability  24h -20°C        GB/T8811             ≤1 %

                               24h  70°C                                                ≤1.5%

Water absorption                                  GB 8810                 ≤3%

Oxygen index                                         GB 8624                 ≥26