Specifications

use water as blowing agent,environmental protection
low density ( 8~10kg/m3), open cell
good performance of shockproof

 

1.Introduction 

 

 

 Rigid polyurethane blend polyols foam system for Packaging  is a mixture of high activity, high molecular weight polyether poyol and different kinds of catalyst,blowing agent and other materials.  

 

 React with Isocyanate to produce the foam which can absorb shock when impacted, it has excellent performances of shockproof and shock absorption.

 

 It applies to precision instrument, apparatus, medical instrument, optical instrument, crafts, fragile goods, glasswares and other goods foaming in site.   

 

 

 

2.Physical Properties 

Items	DBZ-502
Appearance	Light yellow transparent liquid
Viscosity(25°C)        mPa·s	400-600
Specific gravity(20°C)    g/cm3	1.05±0.02
Storage temperature        °C	10-25
Storage life                month	6
Recommended Ratio
	pbw
DBZ-502(POL) Isocyanate(ISO)	100 100

 

 

3.Reactivity Characteristics component temperature 20±2°C)

 

actual value varies depending on process conditions

Cream time         s	10-15
Gel time            s	50-70
Tack free time       s	70-90
Free density      kg/m3	8-10

 

4.Foam Performances 

Recovery rate compressive by 50%     %	≥90
Compressive strength              MPa	≥0.05

 

The values above are typical which are measured by our company. To our products, the data included in the legal field has no constraints.