Specifications

Rigid Polyurethane Blend Polyols Foam System for Spray Insulation
Blowing agent is 365mfc/245fa
Fine and uniformity cells

Product Introduction

Rigid Polyurethane Blend Polyols Foam System for Spray Insulation

DQT-501C is spray blend polyols, blowing agent is 365mfc/245fa instead of HCFC-141B, it reacts with isocyanate to produce foam which has excellent performances, which are as follows,

  1) fine and uniformity cells

  2) low thermal conductivity

  3) perfect flame resistance

  4) good low temperature dimensional stability. 

 

It applies to all kinds of thermal insulation engineering which uses the spray technology, such as cold rooms, pots, large-scale pipelines and construction metope etc.

 

Physical Properties

 

Appearance                   Hydroxyl Value                mgKOH/g Dynamic Viscosity (25 °C)       mpa.s Specific gravity (20 °C )           g/ml Storage Temperature             °C Storage Stability               month

Pale yellow to brown viscous liquid 200-300 100-200 1.12-1.20 10-25 6

 

Recommended Ratio

 

	pbw
DJD-105  blend polyols Isocyanate	100 100-105

 

Reactivity Characteristics

 

(The temperature of the system is 20°C,and the exact value varied depending on processing condition) 

 

Cream Time                  s Gel Time                     s

3-5 6-10

 

Foam Performances

 

items	Test Method	Index
Spray Density                 Closed-cell Rate           Initial Thermal Conductivity(15°C)        Compressive Strength Adhesive Strength    Elongation at break Dimentional Stability  24h  -20°C        24h   70°C  Water Absorption                      Oxygen Index	GB 6343 GB 10799 GB 3399 GB/T8813 GB/T16777 GB/T9641 GB/T8811   GB 8810 GB 8624	≥35kg/m3 ≥90%      ≤24mW/(m.K)  ≥150kPa  ≥120kPa ≥10% ≤1% ≤1.5% ≤3% ≥26

 

 The data provided above are typical value, which are tested by our company. For our company's products, the data included in the law do not have any constraints.