SSiC Ring
USD $10 - $100 /Piece
Min.Order:50 Pieces
SSiC Seal Ring
SSiC ceramic was made from ultra-fine and high purity SiC powder with a small quantity of sintering aids. Under inert gas or vacuum atmosphere of barometric pressure
Pressureless Sintering Silicon Carbide Products (S-SiC)
SSiC ceramic was made from ultra-fine and high purity SiC powder with a small quantity of sintering aids. Under inert gas or vacuum atmosphere of barometric pressure, the materials were sintering under high temperature (1950~2100℃), the ceramic products which with the features of excellent mechanical properties (smooth, wear-resistant, etc.) and chemical properties (stable, high corrosion resistance, etc.), were almost completely dense. Be different to SiSiC, SSiC ceramics do not contain free silicon and metal adhesives which are easily to corrosion, and as it was formed by uniform and dense SiC, thus it has achieved superior performance in strong acid and alkali environment. On sliding interface of SSiC sealing article, independent and discontinuous spherical pores(50±μm) can be used as fluid or storage of lubricants on the surface of sliding elements. It can improve the performance of sliding interface to keep the fluid film bearing, which promote the friction performance of SSiC products.
Excellent corrosion resistance and superior frictional advantages make SSiC to be a wise choice of application in industrial sealing surface. SSiC can be applied in the field of chemical processing, waste water, petroleum refining, paper and pulp, mining, ocean, nuke industry, household appliances, etc.
Sealing Rings Types | Reaction Bonded SiC | Pressureless Sintering SiC | Hot Pressed Sintering SiC | |||
Specifications | SiSiC | SSiC | HPSiC | |||
SSiC-A | SSiC-B | SSiC-C | ||||
Density | G/Cm3 | >3.03 | >3.08 | >3.20 | 2.65-2.95 | >3.15 |
Hardness | HV0.5 | / | >2200 | >2200 | / | >2500 |
HRA | >90 | >92 | >92 | / | >93 | |
HS | / | / | / | >85 | / | |
Bending Strength | Mpa | >350 | >400 | >500 | >150 | >550 |
Compressive Strength | Mpa | >2000 | >2000 | >2200 | >1500 | >2200 |
Elastic Modulus | Gpa | 350 | 400 | 420 | 120 | 420 |
Thermal Expansion Coefficient | 10-6/℃ | 4.0 | 4.0 | 4.2 | 3.0 | 4.0 |
Thermal Conductivity | W/M·k | 50-100 | 90-100 | 60 | 120 | 120 |
Free Silicon Content | % | <12 | - | |||
SiC Purity | % | >98 | ||||
Components | SiC Si C | SiC B4C C | SiC YAG | SiC C | SiC B4C C |
SSiC Sealing Ring
SSiC Sealing Ring | |
SiC | 99% Min |
Density | 3.12g/Cm3min |
Open Porosity | 1%Max |
Bending Strength | 440(1700℃)MPa |
Compressive Strength | 2400(1700℃)MPa |
Coefficient Of Thermal Expansion | 4.2 K-1x10-6 |
Thermal Conductivity | 60 W/M.K(1700℃) |
Application Temp. | 1600-17000C |
SSiC Flat Ring
Advantages
1.Highly-knowledgeable equipment and application expertise
2.Technical innovation in mechanical seal design
3.Design qualification and Design team
4.Simulation and Rotating balance testing
5.Reliable, customer-tailored, sealing solutions
6.Rapid and effective Reaction on feedback
Application
Packing
Workshop
Payment & Delivery
Company Honor
Contact
Contact
Tel: 0086-136-33852636
Email: caec.sara@gmail.com
Sales Manager: Sara Wang
Henan Si&C Co., Ltd