Hastelloy G-3 (UNS N06985)
Negotiable /Kilogram
Min.Order:50 Kilograms
Danyang HB Special Alloy Co.,Ltd
*Similar Grade
GB | Trademark | UNS | DIN EN/DIN | W-Nr. |
NS3403 | Hastelloy G-3 | N06985 | Nicrofer 4023 hMo | 2.4619 |
*Product Forms
Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire
*Brief
A nickel-chromium-iron alloy with additions of molybdenum and copper. It has good weldability and resistance to intergranular corrosion in the welded condition. The low carbon content helps prevent sensitization and consequent intergranular corrosion of weld heat-affected zones. Used for flue-gas scrubbers and for handling phosphoric and sulfuric acids.
*Chemical Composition,%
% | Ni | Mo | Fe | W | Cr | C | Mn | Si | P | S | Co | Cu | Nb |
Min | Rest | 6.0 | 18.0 | 21.0 | 1.5 | ||||||||
Max | 8.0 | 21.0 | 1.5 | 23.5 | 0.015 | 1.00 | 1.50 | 0.025 | 0.015 | 5.00 | 2.5 | 0.5 |
*Typical Physical & Mechanical Property(Annealed)
Density | Melting point | Tensile strength, MPa | Yield strength, MPa | Elongation,% |
8.31 g/cm3 | 1300-1350℃ | 690 | 320 | 50 |
*Specification
Rod, Bar, Wire, Forgings | ASTM B335/ASME SB335 |
Plate, Sheet, Strip | ASTM B333/ASME SB333 |
Pipe, Tube | ASTM B619/ASME SB619, ASTM B622/ASME SB622, ASTM B626/ASME SB626 |
Others | ASTM B366/ASME SB366, DIN17742, ISO4955A |
*Feature
Hastelloy G-3 is a chemically stable and high-temperature resistant alloy, which is well weldable and has a good stability against grain border corrosion in welded condition. Alloy 2.4619 (alloy G-3) is used in flue gas scrubbers, and with phosphoric acid and sulphuric acid. Our product range in 2.4619 (alloy G-3) are tubes and pipes, fittings and flanges, accessories.
*Application
Hastelloy G-3 is a modified version of Hastelloy G in that the higher molybdenum and tungsten contents give this alloy improved corrosion resistance to the welded heat-affected zone. Applications are similar to those for Hastelloy G. Process equipment for flue gas scrubbers, sulfate compounds, mixed acids.