*Similar Grade

*Product Forms

Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire

*Brief

Hastelloy X is a nickel-chromium-iron-molybdenum alloy with an exceptional combination of high temperature strength, oxidation resistance and fabricability. It shows good ductility after prolonged exposure at temperatures up to 870℃ for 16000 hours. It also has excellent resistance to stress corrosion cracking in petrochemical.

*Chemical Composition,%

*Typical Physical & Mechanical Property(Annealed)

*Specification

*Feature

Alloy X is known for its excellent high temperature strength withstanding up to 2200°F. The alloy can also be easily fabricated with forming and welding characteristics by both manual and automatic methods. Additionally, Alloy X is corrosion resistant, heat resistant and oxidation resistant, being able to withstand reducing or neutral atmospheres and oxidation.

*Application

HASTELLOY X finds use in petrochemical process equipment and gas turbines in the hot combustor zone sections. Also used for structural components in industrial furnace applications because of the excellent oxidation resistance.

HASTELLOY X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operating for 8700 hours at 2150 Deg. F. Furnace trays, used to support heavy loads, have been exposed to temperatures up to 2300 Deg. F. in an oxidizing atmosphere without bending or warping. Alloy X is equally suitable for use in jet engine tailpipes, afterburner components, turbine blades, nozzle vanes, cabin heaters, and other aircraft parts.

Gas turbine combustion cans and ducting, heat-treating equipment.

Alloy X has wide use in gas turbine engines for combustion zone components such as transition duct, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Furnace rolls of this alloy were still in good condition after operating for 8,700 hours at 2150 degrees F (1177 degrees C). HASTELLOY X is also used in the chemical process industry for retorts, muffles, catalyst support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.

Useful Properties for Aircraft and Furnace Parts - HASTELLOY X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operation for 8,700 hours at 2150 Deg. F (1177 Deg. C).