1 General description

The main ingredient is water-base inorganic silica , mixed with corrosion protection assistant.The product cost is low.

2 Perfomance charcteisic

The coating layer is smooth, weak acid and alkali resistant, can be adjusted to any colour with paint.

3 Main Technical Data

No.	Item	Data	Test method
1	Appearance	Silver grey Silver grey	GB1721
2	non-volatile %	30	GB/1725
3	coating thickness(μ)	First coating≥15	magnetic gauge
4	Adhesion≤	2	GB1720
5	Flexibility(mm)≤	3	GB/T1731-93
6	hardness	0.7	GB/T1730-93
7	impact resistance(KG.CM)	50	GB/T1732-93
8	wet and heat(h)	240	GB/T1743

4 Instructions and attention:

Dip coating,Spray coating etc.
It should be stirred fully befor usage; distilled water or deionized water can be used to adjust viscosity ;Operating viscosity:30-60s.
When the environment humidity higher than 85%,can add certain industrial alcohol to adjust viscosity
Curing condition: 80℃/10min+140℃/30min
Cleaning appliance: running water can be used
Avoid acid substances, or polymerization and deterioration will happen.
This product can be used alone,the coated surface request oil free,dust free and dry,the better make pre-treatment of degreasing,derusting,and phosphating.

5 Package,storage and transportaion

Package:50kg/ plastic barrel
Storage: 6 month, More than 6 menstrual tests can be used after passing
Transportation: Follow the regulations of commom goods

6 Process

Processing method:
A 1 base-coat+ 1 Top coat
B 2 base-coat+ 1 Top coat (heavy corrosion protection)

Process Parameter

Dip Coating Temperature RT

Operateing Viscosity 45-60 S

Centrifuge 210~270 RPM/min 10s X 4-8 times

( Centrifuge device can not be mix used with spin dyrer )

Spray Coating Temperature RT

Operateing Viscosity 30~40 S

Curing: 80℃ 10min + 140℃ 20—30min

Corrosion protection of b process flow

Corrosion resistance: ≥1500h (NSS)