Wear-resistant Castings, buy 118J Impact Value Wear-resistant Castings For SAG Mills And AG Mills DF017 on China Suppliers Mobile

Product Details

Delivery Time:It depends on quantity to be ordered.

118J Impact Value Wear-resistant Castings For SAG Mills And AG Mills DF017

Quick Details

Mn Steel Liner Casting Feature:

1.The series include Mn13, Mn13Cr2 and Mn18Cr2.
2.Materials conform to GB/T 5680-1998, DL/T 681-1999, JIS G 5153-1999, ASTM A 128

Mn Steel Liner Casting Description:

1. Alloy: The series include Mn13, Mn13Cr2 and Mn18Cr2.

2. Application: It is applicable to the working condition of strong impact, such as teeth plates, concaves and mantles of crushers and excavator bucket teeth and mill liners for SAG mills and AG mills.

3. Microstructure: Austenite or Austenite + little Carbide

4. Hardness: Less than HB300

5. Impact Value: more than 118J

6. Tensile Strength: more than 685 Mpa
7. International Standard: GB/T 5680-1998, DL/T 681-1999, JIS G 5153-1999, ASTM A 128.

China mn steel casting supplier provides mn steel hammer castings services to worldwide mn steel liner casting customer. Hope you find our mn steel casting process and steel casting product description helpful.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5	≤0.5	0.10~3.0	0.10~3.0	≤1.0	≤0.10
Cu	0.10~0.60	≤0.25	0.20~0.40	0.10~1.00	0.10~1.00	-	-
Ni	≤0.50	≤0.30	0~0.30	0~0.30	0~0.30	-	3.3~10
Re	≤0.02	≤0.02	≤0.02	-	-	-	-
Equivalent Specifications	DL/T 681-1999 GB/T26651-2011	AS 2074 L2B Mod	DL/T 681-1999	GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401.	GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12	GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A
Material Type	Martensite Steel	Martensite or Pearlitic Cr Mo Steel	Martensite Steel	Martensite matrix	Austenitic Mn Steel	-
Hardness	HRc≥48	HB470 & HB 321~370	HRc≥50	HRc≥56	HB≤300	HRc≥56
Impact Value	Ak≥40J	-	Ak≥10J