1. Alloy: 15%Cr, 18%Cr and 20%Cr and 26%Cr.
2. Hardness: HRC52-65.
3. The series are designed for high abrasion performance.

High Cr White Iron Hammer Castings Description:

A. The series are designed for high abrasion performance.The anti-wear property is four times as much as that of high manganese steel and twice of low alloy steel.

B. HRC52-65, AK5-15J.

C. The materials conform to:

    GB/T 8263-1999,

    BS4844 3 E,

    AS2027 CrMo 15/3,

    AS2027 CrMo 20/2/1,

    AS 2027 Cr27,

    ASTM A532 Class III type A 25% Cr,

    ASTM A532 class III type A 25%Cr,

    ASTM A532 class II type B 15%Cr-Mo.

D. Assembling face is machined.

 

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5