Cr12 Iron High Cr Iron Castings Cement Mill Liners , Shell Liners DF022  Specifications

High Cr Castings Shell Liners Feature:

1.The series are designed for high abrasion performance.
2.HRC52-65, AK5-15J.
3.The materials conform to GB/T 8263-1999.
 

High Cr Castings Shell Liners Description:

The series are designed for high abrasion performance.
The antiwear property is four times as much as that of high manganese steel
and twice of low alloy steel.
HRC52-65, AK5-15J.

The materials

The materials conform to GB/T 8263-1999,
BS 4844 3E,
AS 2027 CrMo 15/3,
AS 2027 CrMo 20/2/1,
AS 2027 Cr27,
ASTM A532 Class III type A 25% Cr,
ASTM A532Class II type B 15% Cr-Mo.

 

In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.

Technical Parameters

Wuxi Orient Anti-wear Engineering Co., Ltd.

                              Chemical Composition & Mechanical Property of Wear-resistant Castings

Item	Cr-Mo Alloy Steel I	Cr-Mo Alloy Steel II	Cr-Mo Alloy Steel III	High Cr white iron	High Cr Alloy Steel	High Manganese Steel	Ni-Hard cast iron
C	0.30~0.50	0.65~0.90	0.40~0.90	2.40~3.20	1.1~2.2	0.90~1.30	2.40~3.60
Si	0.50~1.20	≤0.75	0.70~1.20	0.60~1.20	0.60~1.20	≤0.08	≤0.80
Mn	0.40~1.20	0.50~1.20	0.60~1.00	0.50~1.00	0.50~1.00	11.00~18.00	≤2.0
Cr	1.70~2.50	1.50~2.50	4.00~7.00	12.00~30.00	11.00~30.00	1.50~2.50	1.5~10
S	≤0.04	≤0.06	≤0.04	≤0.04	≤0.04	≤0.04	≤0.15
P	≤0.04	≤0.06	≤0.06	≤0.06	≤0.06	≤0.06	≤0.15
Mo	≤0.5	≤0.5	≤0.5	0.10~3.0	0.10~3.0	≤1.0	≤0.10
Cu	0.10~0.60	≤0.25	0.20~0.40	0.10~1.00	0.10~1.00	-	-
Ni	≤0.50	≤0.30	0~0.30	0~0.30	0~0.30	-	3.3~10
Re	≤0.02