Delivery Time:20-60 working day

Cold Rolled Coils, Incoloy800H / NS112 / N08810 / NA15(H) / X5NICrAlTi32-20 / 1.4876

Incoloy800H/ NS112/ N08810/ NA15(H)/ X5NICrAlTi32-20/ 1.4876  T0.1-1.0mm W 4-250mm Surface 2B HV 240-280 (Or Customized)                    

Similar Grades:

GB/T	UNS	Trademark	W.Nr
NS112	N08810	Incoloy800H	1.4876

The Incoloy 800H metallographic structure:

800H for the face-centered cubic lattice structure. Ti: C ratio very low carbon content and improve the stability of the structure and allergy resistance as well as resistance to intergranular corrosion. The low temperature annealing around 950 ℃ to ensure a fine grain structure.

Applications:

Incoloy 800H Application field:

1 Nitric acid condenser - nitric acid corrosion resistance

2 Steam heating pipe - good mechanical properties

3. Heating element tube - Very good mechanical properties

Environment to be used up to 500 ° C, the alloy supplier states annealed.

Specifications:

Thickness:0.1—1.0mm 

Width:4.00—250mm 

Tolerance: 0.01mm.

Other specifications can be customized

Surface:2B

Hardness:240—280HV(As order’s requirements)

MOQ:1 tons

Port of Loading:Shanghai

Chemical Composition:

Alloy	%	Ni	Cr	Fe	C	Mn	Si	Cu	S	Al	Ti	P
Incoloy 800H	Min	30	19	Margin	0.05					0.15	0.15
Max	35	23	0.10	1.5	1	0.75	0.015	0.60	0.60	0.03

Physical Properties:

Density	8.0 g/cm3
Melting point	1350-1400 ℃

Mechanical Character:

Condition	Tensile strength Rm N/mm2	Yield strength RP0.2 N/mm2	Elongation As %
Solid solution	450	180	35

Competitive Advantage:

1Having excellent corrosion resistance in the aqueous medium of the extremely high temperatures of up to 500 ℃

2 Good resistance to stress corrosion performance

3 very good workability

Corrosion resistance of Incoloy 800H:

800H resistant to many corrosive media corrosion. Its high nickel content so that it has a good resistance to stress corrosion cracking in aqueous corrosion conditions. The high chromium content has better resistance to pitting and crevice corrosion cracking. The alloy has good resistance to nitric acid, organic acid corrosion, but limited corrosion resistance in sulfuric acid and hydrochloric acid. In addition to pitting corrosion may occur in the halide, good corrosion resistance in oxid