2B Inconel 600 / NS312 / N06600 / NA14 / NC15Fe / 2.4816 T0.1-1.0mm Cold Rolled Coils

Inconel 600/NS312/N06600/NA14/NC15Fe/2.4816    T0.1-1.0mm W 4-250mm Surface 2B HV 240-280 (Or Customized)           

Similar Grades:

GB/T	UNS	Trademark	JIS	W.Nr
NS312	N06600	Inconel600	NCF600	2.4816

Inconel 600 corrosion resistance:

600 alloy corrosion resistance for a variety of corrosive media. Chromium component under oxidizing conditions so that the alloy (alloy 200), and nickel than nickel 99.2 99.2 (alloy 201, a low-carbon), having a better corrosion resistance. In the same time, the higher the nickel content of the alloy with good corrosion resistance in reducing conditions and alkaline solution, and can effectively prevent the chlorine - iron stress corrosion cracking. Of organic acids such as acetic acid, acetic acid, formic acid, stearic acid, the 600 alloy has good corrosion resistance, and the inorganic acid having a moderate corrosion resistance. Primary and secondary loop used in high purity water in a nuclear reactor having a very excellent corrosion resistance. 600 particularly outstanding performance is the ability to resist corrosion of dry chlorine and hydrogen chloride, the application temperature of 650 ° C. At high temperatures, the alloy in the annealed and solution-treated state air has good antioxidant the spalling properties and high strength. The alloy may also be resistant to ammonia and nitriding, carburizing atmosphere, but when the redox conditions change alternately, an alloy will be the corrosion of the part of the oxidizing medium (such as Green Death solution).

Applications:

1. Erosion atmosphere thermowell

2.Vinyl chloride monomer production: anti-chlorine, hydrogen chloride, oxidation and carbonation corrosion

3.Uranium oxidation converted into hexafluoride: anti-hydrogen fluoride corrosion

4 In the production and use of corrosive alkali metal, especially the use of sulfide environment

5. Titanium dioxide with chlorine legal system

6.Production of organic or inorganic chlorides and fluorides: anti-chlorine and fluorine gas corrosion

7 nuclear reactors

8 retorts in the heat treatment furnace and components, especially in the carbonizing and nitriding atmosphere

9. The catalytic regenerator in petrochemical production applications above 700 ℃ recommended alloy 600 in order to get a longer service life.

Specifications:

Thickness:0.1—1.0mm 

Width:4.00—250mm

Tolerance: 0.01mm.

Other specifications can be customized

Surface:2B

Hardness:240—280HV(As order’s requirements)

MOQ:1 tons

Chemical Composition:

Alloy	%	Ni	Cr	Fe	C	Mn	Si	Cu	P	S
600	min	72	14	6
max		17	10	0.15	1	0.5	0.5	0.015	0.015

Physical Properties:

Density	8.4 g/cm3
Melting point	1370-1425 ℃

Mechanical Character:

Condition