Customized Cold Rolled Coils,Hastelloy C /NS333 T0.1-1.0mm W 4-250mm Surface 2B HV 240-280

Description:

HastelloyC processing performance

Thermal processing

Thermal processing temperature range of 1200 ℃ ~ 950 ℃, cooling water-cooled or air-cooled fast.

In order to ensure the best performance of anti-corrosion, thermal processing should be subjected to heat treatment, the workpiece should be added directly been warming

Heat-treating furnace.

Cold working process

Work hardening rate than austenitic stainless steel, so the need for processing equipment selection. Workpiece should be solution heat treatment state, there should be intermediate annealing and cold rolling process.

2. Cold deformation is greater than 15%, is required on the workpiece for the second solution treatment.

Welding process

Suitable for using any conventional welding processes welding, such as tungsten electrode inert gas welding, plasma arc welding,, handmade sub-arc welding, metal inert gas welding, metal inert gas shielded arc welding.

Applications:

1.Nuclear power industry

2.Chemical industry, oil industry

3.The container heat exchangers, plate cooler

4.Reaction of acetic acid and acidic products

5.High-temperature structural parts

Specifications:

Thickness:0.1—1.0mm 

Width:4.00—250mm 

Tolerance: 0.01mm.

Other specifications can be customized

Surface:2B

Hardness:240—280HV(As order’s requirements)

MOQ:1 tons

Port of Loading:Shanghai

Chemical Composition:

Alloy	%	Ni	Cr	Mo	Fe	Wo	Co	C	Mn	Si	V	P	S
HastelloyC	Min	Margin	14.5	15	4	3
Max	16.5	17	7	4.5	2.5	0.08	1	1	0.35	0.04	0.03

Physical Properties:

Density	8.94 g/cm3
Melting point	1350 ℃
Specific heat capacity	0.385 103J/kg•K
Thermal conductivity	29.3 W(m•K)
Elastic modulus	210 103MPa

Mechanical Character:

Condition	Tensile strength Rm N/mm2	Yield strength RP0.2 N/mm2	Elongation As %
Cold rolled sheet	690	285	40
Cold rolled strip	690	315	30

Competitive Advantage:

HastelloyC corrosion resistance

1.Corrosion resistance in a sulfuric ac