Specifications

1. High fluidity and good capillarity.
2. Low silver content

Main applications

Brazing alloy with 1% Ag

Factory Destination: HZ-Ag1B

This high quality welding and brazing alloy is an alloy of copper and zinc with small addition of silicium, silicon, nickel and manganese to assist deposition. This addition refines the alloy--HZ-Ag1B, lowers the melting range, improvingelectrical conductivity and increasing ductility.

Having a slightly lower melting range, is recommended for the brazing of galvanized steels, while protecting the zinc coat. Itshigh fluidity and good capillarity makes it suitable for brazing tricky works.

Heating can be achieved by induction, torch or by furnace.
Most used in lock-smithing and work shops.
A flux is necessary. 

 

EN ISO 3677: B Cu 59 Zn Ag Si 850-870

Parameters	Analysis	Properties	Ø x L (mm)	manufacturer
Melting range:  850-870 ° C	Cu: 58.0% Zn: balance Ag: 1.0% Others: Si,Mn,Sn	Rm: 480 Mpa A: 30% d: 8,5 g/cm³	Bare and rods Ø 1,5 - 2 - 2,5 - 3 - 4 mm, standard length 500 mm and 1000mm. Wire:0.3-4.0mmAlso available in wire, ring strip and performs.	HUAZHONG