Specifications

E309LT1-1 Stainless welding wire suitable for welding of 22%Cr-12%Ni steel (SUS 309S), 18%Cr-8%Ni clad steel and dissimilar m

1)AWS E309LT1-1/-4 Stainless steel Welding wire

E309LT1-1 is a kind of stainless steel gas-shielded flux cored welding wire.

E309LT1-1/4 is suitable for welding of 22%Cr-12%Ni steel (SUS 309S), 18%
Cr-8%Ni clad steel and such as Cr-Mo steel or mild steel to stainless and
build-up welding of carbon steel. E309LT1-1/4 is a flux corded wire for Flat, H-Fillet, V-up, down
position welding for CO2 or Ar-CO2 (75%Ar-25%CO2) shielding gas. It provides excellent
usability with stable arc, less spattering, good bead appearance. For mechanized welding of HFillet
this wire is an excellent choice, as it meets the requirement of superior wire feeding
properties combined with high deposition efficiency.

2)Shielding Gas: CO2 or Ar+(20~25)%CO2

Diameter: 1.2-1.6mm

3)Standards:

a) AWS E309LT1-1

b) GB E309LT1-1

C) YC-YA309L(Q)

4)Packing:

One spool is vacuum packed by aluminum film and then one carton

Chemical composition of deposited metal(%)
C	Mn	Si	S	P	cr	Ni
0.028	1.35	0.75	0.001	0.025	22.04	12.21

6)Mechanical Properties of Deposited Metal:

TensileStrength:560MPA,Elongation:38%

STAINLESS WELDING WIRE

Product Name	Specification			Chemical Composition of Deposited Metal%						Mechanical Properties of Deposited Metal		Characteristics and Applications
Product Name	GB	AWS	JIS	C	Si	Mn	S	P	Other	σ_b (MPa)	₅ (%)	Characteristics and Applications
YC- YA308(Q)	E308T1-1	E308T1-1	YF308C	0.058	0.58	1.31	0.011	0.021	Cr19.80 Ni9.80	590	38	Used for welding 18Cr-8Ni stainless steel.
YC- YA308L(Q)	E308LT1-1	E308LT1-1	YF308LC	0.03	0.58	1.40	0.011	0.020	Cr20.20 Ni10.30	565	40	Used for welding low C-18Cr-8Ni stainless steel.
YC- YA309L(Q)	E309LT0-1	E309LT0-1	YF309LC	0.03	0.50	1.35	0.012	0.020	Cr23.50 Ni13.00	580	42	Used for welding extra low carbon stainless steel 00 Cr23Ni13.It has more excellent resistance to the intercrystalline.
YC- YA309MoL(Q)	E309LMo T0-1	E309LMo T0-1	YF309MoC	0.035	0.59	1.12	0.012	0.018	Cr21.50 Ni12.30 Mo2.20	570	32	Used for welding extra low carbon stainless steel 00 Cr23Ni13 Mo2.It has excellent corrosion-resistance .
YC- YA347L(Q)	E347LT1-1	E347LT1-1	YF347LC	0.03	0.60	1.45	0.015	0.02	Cr19.80 Ni9.80 Nb0.40	650	40	Used for weldingimportant corrosion-resistant low carbon Cr19Ni11Ti stainless steel. It has excellent corrosion-resistance to the intercrystalline.
YC- YA316L(Q)	E316LT0-1	E316LT0-1	YF316LC	0.03	0.50	1.45	0.013	0.02	Cr19.00 Ni12.50 Mo2.40	580	38	Used for welding low C-18%Cr-12%Ni-2%Mo stainless steel.
YC- YBG217(Q)	E410NiMo T0-1			0.05	0.90	0.78	0.008	0.012	Cr11.50 Ni4.50 Mo0.44	810	18	Used for welding 0Cr131 Cr132 Cr13 stainless steel.
YC- YBG217W(Q)	E410NiMo T1-1			0.05	0.90	0.78	0.008	0.012	Cr11.50 Ni4.50 Mo0.44	810	18	Used for welding 0Cr131 Cr132 Cr13 stainless steel.
YC- YBR607(Q)				0.09	0.89	1.00	0.014	0.017	Cr10.80 Ni0.89 Mo0.65 V0.21 Cu0.20	759	18	Used for welding 1 Cr11MoV stainless steel.
YC- YBG317(Q)				0.028	0.90	0.78	0.008	0.012	Cr16.50 Ni5.50 Mo0.44	880	18	Used for welding of corrosion-resistant nitric acid, heat-resistance stainless steel Cr17 .
YC-YBG317W(Q)				0.024	0.90	0.78	0.008	0.012	Cr16.50 Ni5.50 Mo0.44	910	17	Used for welding of corrosion-resistant nitric acid, heat-resistance stainless steel Cr17