This flux cored wire is Used for welding atmospheric corrosion-resistance steel.

 

YC-YL457(Q)  was developed for out-of-position welding. This flux cored wire
will deposit out-of-position welds at substantially higher welding currents than other stainless steel flux cored wires, resulting in a higher deposition rate. The slag is selfpeeling and minimizes cleanup.

 

YC-YL457(Q)   was formulated for use with 75% Argon/25% CO² shielding gas; however, straight CO² may also be used. The 75/25 mixture will produce a smooth arc with virtually no spatter and slightly higher yield and tensile strengths than CO². The mechanical properties and deposit analysis
will meet AWS 5.22 specifications with either gas.

 

                                                                                                                                 

Packing:

spool+carton+pallet

One spool is vacuum packed by aluminum film and then one carton 

 

 

 

 

Chemical composition of deposited metal(%)
C	Mn	Si	S	P	Cr	Ni
0.05	1.23	0.37	0.012	0.016	/	0.41

 

Mechanical Properties of Deposited Metal:

 

TensileStrength:590MPA,Elongation:36%

 

 

 

  Chemical Composition of deposited metal

Item	Yield Point   (MPa)	TensileStrength   (MPa)	Elongation   (%)	Charpy V-notch Impact Toughness
				Test Temp. (°C)	Impact Energy (J)	Average (J)
Standard	470	≥520	≥35	-40	80	/

 

 Size and Recommended Current (DC-) and Voltage Range

Size	Voltage Range	Current (DC-)
1.2MM	18~30V	150~280A
1.6MM	20~32V	170~320A

  Procedures may vary with change in position, base metals, filler metals,equipment and other changes.

 

Shielding Gas: CO2 or70% Ar+CO2

 

 

Stainless steel flux-cored wires  

 

 YC-YL457(Q) 

Available Diameters:

1.0mm/1.2mm / 1.6mm 

 

 

Shielding Gas:CO2 or75% Ar+CO2

 

 

 