Imported anti static POM board, anti static POM rod, anti static voltage rod, anti static polyformaldehyde board. Anti-static POM board with polyformaldehyde as the base material, adding carbon filler material, its impedance value is stable, in the field of application of antistatic materials show high performance characteristics: Anti-static POM board of all parts of the anti-static value is the same, the overall resistance value is 106-109Ω mechanical processing or surface wear, anti-static value no change resistance to organic solvents, room temperature is not dissolved, low temperature performance and best, the use of temperature -40-90℃ anti-friction and anti-diving excellent, high mechanical strength, high rigidity and hardness. Good sliding performance, no water absorption, high mechanical strength, excellent processing performance.

Color: Natural/black

The specifications of the POM plate size: 0.5 mm - 100 mmx1000 mmx510/610/2000 mm

POM plate size: 5-300mm

Color: Natural/black

Process characteristics:

(1) POM processing can not dry, it is best to preheat in the process of processing (800℃ or so), the stability of product size is good.

(2) The processing temperature of POM is very narrow (0 ~ 215℃), and when the residence time in the barrel is slightly longer or the temperature exceeds 220℃, it will decompose and produce irritating formaldehyde gas.

(3) When the POM material is injected, the pressure holding pressure should be larger (similar to the injection pressure) to reduce the pressure drop. Screw speed can not be too high, the residual amount should be less;

(4) POM product shrinkage rate is large, easy to produce shrinkage or deformation. POM specific heat, high mold temperature (800 ~ 100℃), the product is very hot when demoulding, need to prevent burning fingers.

(5) POM should be formed under the conditions of "medium pressure, medium speed, low material temperature and high die temperature", and the mold temperature should be controlled when precision products are formed

(6) With high mechanical strength and rigidity

(7) The highest fatigue strength

(8) Environmental resistance, good resistance to organic solvents

(9) Strong repeated impact resistance, good electrical properties, good resilience, with its own lubrication, good wear resistance, excellent dimensional stability.

Guangzhou Yayan Plastic Products Co., LTD. Spot supply: PEEK board/rod, PPS board/rod, PVDF board/rod, PTFE board/rod, PSU board/rod, PEI board/rod, PI board/rod, PAI board/rod, PPO board / Rod, PBT board/rod, CPVC board/rod, UPE board/rod, PETP board/rod, PC board/rod, POM board/rod, ABS board/rod, PMMA board/rod, PP board/rod, PE board / bar, imported PU board/bar, German PES board/bar, domestic PVC board/bar, Swiss engineering PBI board/bar, German PA nylon series board/bar/sheet, MC nylon series board. Insulation materials: Taiwan red, black electric board, cold drawing board, phenolic laminate cloth bar board, heat insulation board, epoxy glass fiber bar board, epoxy board (FR-4) asbestos board, etc. Anti-static products: anti-static POM board/rod, anti-static organic board, anti-static PC board. Anti-static PVC plate/bar, anti-static nylon plate/bar synthetic SLATE and so on.

Welcome to visit to negotiate!

Enquiries can be reached at 020-3622 28290

Phone number: 180 2748 2446

QQ: 1006680516

Contact: Miss Huang

POM C/H (black, white) : respectively represents POM copolymer and POM homopolymer, POM copolymer has low melting point, thermal stability, chemical corrosion resistance, flow characteristics, hydrolysis resistance, strong alkali resistance and thermal oxidation degradation, processing property is better than homopolyformaldehyde.

POM homopolymer crystallinity, creep, thermal expansion rate is lower, wear resistance, mechanical strength, rigidity, thermal deformation temperature than copolyformaldehyde. (At present, POM-C copolymerization is widely used in semi-finished POM products on the market)

Pom-h +PTFE (dark brown POM-H+TF is extruded from DuPont POM (DELRIN) and PTFE (Teflon). It retains most of the natural strength of POM-H. Because filled with PTFE (Teflon) fiber and some performance changes, slightly softer, less rigid, more slippery than pure polyformaldehyde resin. Compared with pure POM board, the material lubricity is better. The bearing made of POM-H+PTFE has low friction coefficient, wear resistance and no peristalsis.