Epoxy resin coated insulation paper for trasnformer resist sudden short circuit
USD $4.8 - $4.9 /Kilogram
Min.Order:500 Kilograms
Nantong Rizhi Electric Power Material Co.,Ltd
thickness 0.08mm to 0.5mm diamond dotted insulation paper for transformer coil
China manufacturer of transformer insulation material prepreg DMD paper
Manufacturer of transformer used electrical insulation crepe paper
Chinese manufacturer of flexible insulation material grade H insulation NMN
Manufacturer of transformer insulation material 0.46mm electrical insulation crepe paper
China manufacturer of flexible electrical insulating crepe paper tube for transformer
Epoxy coated insulating paper
The base paper of our new product epoxy coated insulating paper is Tervakoski Tertrans N paper,and coat the special modified epoxy resin on the paper in net shape,then solidified to step B.It’s mainly used in high-low voltage coil and main channel insulation of oil immersed transformers.After winding and baking process,the epoxy coating insulating paper will increase the mechanical strength of the transformers’ coil.Improve the transformers’ ability to resist sudden short circuit.Therefore,the oil immersed transformers will work effectively and safely for long term.
Product Solidification Conditions
First curing under temperature 90℃±5℃ for 3 hours, and then rise temperature to 125℃±5℃ and keep 6 hours to cure;curing in accordance with the provision of both parties is also available.
Storage
Store in a dry,clean and well-ventilated warehouse, and keep away from fire and heat point, also keep away from the sun. The storage period is one year, qualified products exceeding the storage period can still be used.
Specification
No. | Property | Unit | Requirements | ||||||||
1 | Nominal thickness | mm | 0.08 | 0.13 | 0.18 | 0.25 | 0.30 | 0.38 | 0.50 | ||
2 | Single-sided adhesive thickness | um | 10~20 | ||||||||
3 | Content of soluble resin | g/㎡ | ≥15 | ||||||||
4 | Conductivity of water extract | mS/m | ≤12 | ||||||||
5 | Bonding strength | Single side coating | - | Tear the incision of sample,the paper bond firmly with paper,no delamination. | |||||||
Double side coating | MPa | ≥2.5 | |||||||||
6 | Pollution of transformer oil | - | No pollution(tanδ<0.001) | ||||||||
7 | Tensile strength | MD | N/10mmWidth | ≥60 | ≥120 | ≥160 | ≥220 | ≥240 | ≥260 | ≥400 | |
CD | ≥30 | ≥60 | ≥80 | ≥100 | ≥120 | ≥180 | ≥300 | ||||
8 | Tearing strength | MD | mN | ≥450 | ≥900 | ≥1350 | ≥2000 | ≥2600 | ≥3600 | ≥5800 | |
CD | ≥500 | ≥1000 | ≥1500 | ≥2300 | ≥2900 | ≥4100 | ≥6500 | ||||
9 | Breakdown voltage | In air | kV | ≥0.90 | ≥1.40 | ≥2.20 | ≥2.40 | ≥3.20 | ≥3.50 | ≥4.50 | |
In oil | ≥5.20 | ≥7.50 | ≥9.50 | ≥13.00 | ≥17.00 | ≥19.00 | ≥23.00 |
Nantong Rizhi Electric Power Material Co.,Ltd
Add:No.99,Tangang Road,Hai'an High Tech Zone,Nantong City,Jiangsu Province,China.
Shirly Zhu
Mobile:0086-13861918210(wechat)
Fax:0086-88770698
Email:sales06@rzinsulation.com