Material Chrome ASTM A295 Grade 52100 Seamless Bearing Steel Tube / Pipe
USD $1,200 - $1,256 /Ton
Min.Order:10 Tons
Quick Details View All >
Liaocheng Kuncheng Pipe Co., Ltd.
Business Type: Government ministry/Bureau/CommissionMain Products: CARBON STEEL PIPE ,ALLOY STEEL PIPE ,STAINLESS STEEL PIPE ,SQUARE RECTANGULAR TUBE
DIN 17230 Material 100Cr6 Chrome Bearing Seamless Steel Tube
API 5L Gr.B PSL1,PSL2 Black Ms Oil Pipeline Pipe Seamless Tube ASTM A106Gr.B
Industry Grade ASTM A312 904L High-alloy Austenitic Seamless Stainless Steel Pipe
SA210A1 High Pressure Boiler Seamless Rifled Tube SA213T2,T12 material
ASME SA213 GR.T22 Seamless Rifled Tube/P91 Ribbed Steel Tube for Boiler Pipe
Alloy Material ASTM A333 Grade 6 Seamless Steel Pipe for Low Temperature Service
Product Details
1.Relevant Steel Specification of ASTM 52100 Bearing Steel
| Country | USA | German | Japan | British |
| Standard | ASTM A295 | DIN 17230 | JIS G4805 | BS 970 |
| Grades | 52100 | 100Cr6/1.3505 | SUJ2 | 535A99/EN31 |
2. Chemical Composition of 52100 Bearing Steel and Equivalents
| Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Cu | Mo |
| ASTM A295 | 52100 | 0.93-1.05 | 0.25-0.45 | 0.025 | 0.015 | 0.15-0.35 | 0.25 | 1.35-1.60 | 0.30 | 0.10 |
| DIN 17230 | 100Cr6/1.3505 | 0.90-1.05 | 0.25-0.45 | 0.030 | 0.025 | 0.15-0.35 | 0.30 | 1.35-1.65 | 0.30 | – |
| JIS G4805 | SUJ2 | 0.95-1.10 | 0.50 | 0.025 | 0.025 | 0.15-0.35 | – | 1.30-1.60 | – | – |
| BS 970 | 535A99/EN31 | 0.95-1.10 | 0.40-0.70 | – | – | 0.10-0.35 | – | 1.20-1.60 | – | – |
3. Mechanical Properties of ASTM A295 52100 Bearing Steel
| Properties | Metric | Imperial |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Hardness, Brinell | – | – |
| Hardness, Knoop (converted from Rockwell C hardness) | 875 | 875 |
| Hardness, Rockwell C (quenched in oil from 150°C tempered) | 62 | 62 |
| Hardness, Rockwell C (quenched in water from 150°C tempered) | 64 | 64 |
| Hardness, Rockwell C (quenched in oil) | 64 | 64 |
| Hardness, Rockwell C (quenched in water) | 66 | 66 |
| Hardness, Vickers (converted from Rockwell C hardness) | 848 | 848 |
| Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel) | 40 | 40 |
| Properties | Metric | Imperial |
| Density | 7.81 g/cm3 | 0.282 lb/in³ |
| Melting point | 1424°C | 2595°F |
| Properties | Metric | Imperial |
| Thermal expansion co-efficient (@ 23-280°C/73.4- 36°F, annealed) | 11.9 µm/m°C | 6.61 µin/in°F |
| Thermal conductivity (typical steel) | 46.6 W/mK | 323 BTU in/hr.ft².°F |
4. Forging of A295 52100 Bearing Steel
AISI 52100 alloy steel is forged at 927 to 1205°C, and should not be forged below 925ºC. A post-forge equalization treatment is recommended at 745ºC for 4-6 hours followed by air cooling for SAE/AISI 52100 steel.
5. Heat Treatment for ASTM 52100 Bearing Steel
ASTM/AISI 52100 alloy bearing steel is heated at 816°C followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C followed by slowly cooling in order to reduce the machining stress.
Hot Working
AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.
Cold Working
AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.
Annealing
For spheroidize anneale, the following isothermal anneal is recommended:
Quenching
AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.
Tempering
Temper to desired hardness as indicated by tempering curves after water or oil quench.