High Performance Alloy, description about Nimonic 901 (UNS N09901) on China Suppliers Mobile

Product Details

*Similar Grade

Trademark

UNS

W-Nr.

GH2901

Nimonic 901

Inconel 901

N09901

2.4662

*Product Forms

Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire

*Brief

NIMONIC 901 (UNS N09901/W.Nr. 2.4662) is an age-hardenable Ni-Fe-Cr superalloy with significant additions of molybdenum, titanium and aluminum. The alloying route for this highperformance material may include combinations of vacuum induction melting, vacuum arc remelting and electroslag remelting, according to the final application and the customer’s specification. Typically, the alloy is used for gas turbine engine discs, shafts, rings, casings and seals with a maximum service temperature of around 600°C (1100°F).

*Chemical Composition,%

%	Ni	Cr	Mo	Fe	C	Mn	Si	P	S	Cu	Co	Ti	Al
Min	40.0	11.0	5.0	Rest								2.80
Max	45.0	14.0	6.5	Rest	0.10	0.50	0.40	0.03	0.03	0.50	1.00	3.10	0.35

*Typical Physical & Mechanical Property(Solution Annealed)

Density	Melting point	Tensile strength, MPa	Yield strength, MPa	Elongation,%
8.14 g/cm³	1280-1345℃	≥1034	≥689	≥12

*Specification

Can be made according to customers’ specifications

*Feature

Alloy 901 has high yield strength and creep resistance at temperatures to about 1110°F (600°C). As Alloy 901 has a substantial iron content it enables alloy 901 to combine strength with good forging characteristics.

*Application

Alloy 901 is commonly used for gas turbine engine discs, shafts, rings, casings and seals.