Description:H1060 Epoxy Primer for Galvanization Plates (2K)
Composing:
It is a kind of two components protective primer that is made from diversiform modified resin, rust proofing pigment, shield fillers, hollow micro sphere, and organic solvent with H1160 hardener according to the proportion of 4:1.
Characteristics:
This primer has excellent adhesive force. It can fast dry at normal temperature; it has good capacity of elasticity and extension to deformation generated by the temperature change of substrate, good mechanical character, and excellent salt spray resistance and strong anticorrosive property. Therefore, it is a kind of high performance automobile primer.
Applications:
This product is applied to metal products that have the higher requirement to anticorrosive property, anticorrosive coatings of car body, car frame, car box and car bridge of luxurious cars, as well as the primer of electrolytic plate, galvanized plate, aluminium alloy and other nonferrous metal products and glass fiber reinforced plastic.
Item Technical Index and Inspection Standard:
Index of original primer outward appearance: no foreign matter and obvious granule, easy to homogenize visual measurement
Color and appearance: olivine or sage green thick liquid visual measurement
Involatile constituent (120 degrees Centigrade /1h): ≥60%, GB/T6751
Fineness: ≤35 μm, GB/T1724
H1160 original hardener outward appearance: light yellow transparent liquid visual measurement
Amine value: 135~165mg KOH/g 0.1NHCl titration
Film Coating
Performance index, color and appearance: olivine or sage green, leveling and smoothness visual measurement
Dry time: ≤6h (hard dry in 25 degrees Centigrade), GB/T1728, ≤0.5h (baking dry in 80 degrees Centigrade)
Adhesive force: Grade 1, GB/T9286
Pliability: ≤1mm, GB/T1731
Impact strength: ≥50kg.cm, GB/T1732
Burnishing performance (20 times): easy to Burnishing, not adhibited sandpaper GB/T1770
Nitrocellulose lacquer resistance: not lift, not bleed red visual measurement
Water resistance (168h): not bubble, not rust, GB/T5209
Salt water resistance (264h): not bubble, not peel off, GB/T 1763
Heat and humidity resistance (96h): grade 1, GB/T 1765
Salt spray resistance (216h): Grade 1, GB/T 1765
Reference for construction and notes:
1. It is suitable for spray coating and brush coating, implement the rust removing treatment to substrate before construction (spray sand to grade Sa2.5, surface roughness 30~70μm)
2. Mix well H1060 epoxy primer and H1160 hardener according to the proportion of 4:1, keep curing for 20min (room temperature), uses H1260 thinner to dilute for 18~20s (T-4, 25 degrees Centigrade), wet-to-wet spray painting twice, dry for 6 hours (or 0.5H/80 degrees Centigrade). After drying, scrape putty or spray intermediate primer and finishing paint.
3. Mix paint every time according to construction using amount, the paint that has mixed into hardener should be used up in time (use for 4h at normal temperature), or it will be discarded due to becoming thicker.
4. The storage life is one year from the date of commencement of production (if it is beyond the storage life, please confirm according to the standard inspection; if it is still qualified, it can be continuously used).
Packing and storage:
Packing specification: primer is packed 4L printing iron drums. Hardener is packed 1L printing iron drums.
Storage condition: 5-35 degrees Centigrade, store in a cool, dry well-ventilated place.