DIN 1.2080 Steel Round Bar , Cold Work Tool Steel for Cold Work Mold and Tools

Steel Grade:	1.2080	Application:	Tool Steel, Mold Steel
Shape:	Round bar	Standard:	AISI, DIN, JIS, GB
Dimension:	Φ10 – 600 mm	Surface:	Black, Peeled, Turned, Grinded
Technique:	Hot rolled, Forged	Ultrasonic Test:	100% UT Passed

Description:

◆ Equivalence

AISI / SAE	DIN / W.Nr	JIS	GB
D3	1.2080	SKD1	Cr12

◆ Chemical Composition (%)

1.90

2.20

0.10

0.60

0.20

0.60

≤

0.030

≤

0.030

11.00

13.00

◆ Dimensions

	Hot Rolled	Forged
Diameter (mm)	10-130	60-600
Length (mm)	2000-5800	2000-5800
** We suggest ESR for the size over Φ400mm.

◆ Delivery Condition

EAF+(ESR) or EAF+LF+VD+(ESR), Hot rolled or Forged, Annealed, Hardness≤250HB,

Black surface or Machined surface (Peeled, Turned, Grinded), UT 100% Passed

◆ Characteristics

1. A kind of cold work tool steel widely used, belonging to Ledeburitic steel with high

carbon and high chromium.

2. Quite good hardenability and wearing resistance, and small distortion after quenching.

3. Not good impact toughness, be liable to fracture and form inhomogeneous eutectic

carbides.

◆ Applications

1. Common used for making cold work molds of excellent wearing resistance with

light shock loads, such as punch heads, cold cutting scissors, drill bushes, gauges,

wire drawing sheets, drawing dies, thread rolling dies etc.

2. Making cutting tools which is used for machining material of low hardness.

3. Used as plastic mold with good wearing resistance and long service life.

◆ Forging Technique

Heat

Temperature

Start Forging

Temperature

Finish Forging

Temperature

Cooling Method

1120 - 1140 °C

1080 - 1100 °C

880 - 920 °C

Slow Cooling

◆ Heat Treatment

Annealing

800 to 850°C

Slow controlled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C,

further cooling in air.

Hardness after annealing: max. 250 HB.

Stress relieving

Approx. 650°C

Slow cooling in furnace; intended to relieve stresses set up by extensive machining,

or in complex shapes.

After through heating, hold in neutral atmosphere for 1-2 hours.

Hardening

940 to 970°C

Oil, salt bath (220 to 250°C or 500 to 550°C), compressed or still air if thickness does

not exceed 25 mm and if hardening temperature is on the upper side of the range.

Holding time after temperature equalization: 15 to 30 minutes.

Obtainable hardness: 63 - 65 HRC

Tempering

Slow heating to tempering temperature immediately after hardening/time in furnace

1 hour for each 20 mm of workpiece thickness but at least 2 hours/cooling