Cr-Mo Steel Mill Liners Wear Castings With More Than HRC50 And AK49
Negotiable /Roll
Min.Order:1 Roll
Wuxi Orient Anti-wear Engineering Co.,Ltd.
Cr-Mo Steel Castings Mill Liner Design And Installation With HRC50
High Cr Cast White Iron Castings With 26%Cr Alloy And HRC52-65 Hardness
Mn Steel Casting ,Wear-resistant Castings Crusher Hammer Castings DF053
Highly Alloy Steel Heat Resistant Castings Cooling Machines DF028
Industrial Highly Alloyed Alloy Steel Castings Corrosion Resistant
1. Hardness difference from surface to center is less than HRc2.
2. The series are designed for high abrasion performance.
3. More than HRc50, AK49-88J.
In the recent 20 years, our liners have been widely used in large, medium and small ball mills in Chinese power generation, mining, cement, Chemical engineering and metallurgical industries and super fine pulverizing equipments. It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |
- |
3.3~10 |