Iron Crusher Wear Parts ,Tub Grinder Wear Parts For Ore Mining
Negotiable /Kilogram
Min.Order:1 Kilogram
Wuxi Orient Anti-wear Engineering Co.,Ltd.
High Cr Cast Iron Ball Mill Liners Design And Installation For Industry
Castings Ball Mill Liners Hardness , Chrome Alloy Steel Liners
High Reliability Steel Castings Mine Mill Liner Use For AG Mills DF038
Low Breakage Intermediate Diaphragm / Retention Ring Liners Cement Mill
HRC58 Boltless Ball Mill Liners Grinding Mill CaCO3 Power Plant
Cr-Mo Steel Liners Mill Liner Design And Installation With HRC48
Iron Crusher Wear Parts,Tub Grinder Wear Parts For Ore Mining
Quick Details
Wear Parts for Crusher Feature:
1.Jaw plates for jaw crushers;
2.Hammers and impact plates for impact crushers;
3.Concaves and mantles for cone crushers.
Wear Parts for Crusher Description:
A. Jaw plates and cheek plates for jaw crushers,
B. blow bars and impact plates for impact crushers,
C. cone liners for gyratory crushers,
D. hammers for hammer crushers and concaves and mantles for cone crushers.
Depending on the specific working conditions,all wear parts can be ordered as Manganese Steel,high Cr cast iron or Cr-Mo Alloy Steel.
China crusher wear parts supplier provides crusher spare parts services to worldwide crusher spares customer.Hope you find our rock crusher parts process and impact crusher parts product description helpful.
In the recent 20 years,our liners have been widely used in large,medium and small ball mills in Chinese power generation,mining,cement,Chemical engineering and metallurgical industries and super fine pulverizing equipments.It is the only recommended liner product in the latest standard of the electric-power industry in China.
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
C |
0.30~0.50 |
0.65~0.90 |
0.40~0.90 |
2.40~3.20 |
1.1~2.2 |
0.90~1.30 |
2.40~3.60 |
Si |
0.50~1.20 |
≤0.75 |
0.70~1.20 |
0.60~1.20 |
0.60~1.20 |
≤0.08 |
≤0.80 |
Mn |
0.40~1.20 |
0.50~1.20 |
0.60~1.00 |
0.50~1.00 |
0.50~1.00 |
11.00~18.00 |
≤2.0 |
Cr |
1.70~2.50 |
1.50~2.50 |
4.00~7.00 |
12.00~30.00 |
11.00~30.00 |
1.50~2.50 |
1.5~10 |
S |
≤0.04 |
≤0.06 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.04 |
≤0.15 |
P |
≤0.04 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.06 |
≤0.15 |
Mo |
≤0.5 |
≤0.5 |
≤0.5 |
0.10~3.0 |
0.10~3.0 |
≤1.0 |
≤0.10 |
Cu |
0.10~0.60 |
≤0.25 |
0.20~0.40 |
0.10~1.00 |
0.10~1.00 |
- |
- |
Ni |
≤0.50 |
≤0.30 |
0~0.30 |
0~0.30 |
0~0.30 |
- |
3.3~10 |
Re |
≤0.02 |
≤0.02 |
≤0.02 |
- |
- |
- |
- |
Equivalent Specifications |
DL/T 681-1999 GB/T26651-2011 |
AS 2074 L2B Mod |
DL/T 681-1999 |