Industrial Al2O3 / Alumina Ceramic Tube With Metal Use Temperature 1450
Negotiable /Square Meter
Min.Order:1 Square Meter
Customized Dry Pressing / CIP Aluminum Oxide Ceramic Metal Bonding Tube
High Purity Alumina Ceramic Metal Bonding For Chemical, Textile, Aeronautic Industry
Single hole Aluminum structure oxide ceramic sheath for Mechanical engineer industry
OEM Corundum Ceramic Arc Aluminium Oxide Rectangular Crucible manufactures
High pressure resistance Rubber Ceramic Wear Liner for mining, steel and power industry
high temperature wear and abrasion, corrosion resistance Aluminum Oxide Ceramic Tubes
Industrial Al2O3 / Alumina Ceramic Tube With Metal Use Temperature ≥ 1450℃
Description:
The technic of Ceramic with Metal is: adhere the ceramic and metal part with epoxy resin, according to customer’s demands
The material of ceramic part is 95%/99%/99.7% alumina, forming methods are dry pressing and CIP.
Product size is precise, little warp; joint strength between metal and ceramic is high; the joint area is close.
Applications:
Mechanical,electronics,chemical,textile,aeronautic and other fields.
Specifications:
95%,99%,99.7% Al2O3 Material Parameters:
Item |
Test Condition |
Unit Symbol |
95%Alumina ceramics |
99%Alumina ceramics |
99.7%Alumina ceramics |
The main chemical ingredient |
Al2O3 |
Al2O3 |
Al2O3 |
||
Bulk Density |
g/cm3 |
3.6 |
3.89 |
3.96 |
|
Maximum Use Temperature |
1450℃ |
1600℃ |
1650℃ |
||
Water absorption |
% |
0 |
0 |
0 |
|
ROHS Hardness |
≥85 |
≥89 |
≥89 |
||
Flexural strength |
20° C |
MPa (psi x 103) |
358 (52) |
550 |
550 |
Compressive Strength |
20° C |
MPa (psi x 103) |
2068 (300) |
2600(377) |
2600(377) |
Fracture Toughness |
K(I c) |
Mpa m1/2 |
4-5 |
5.6 |
6 |
Coefficient of thermal expansion |
25-1000° C |
1X 10-6/°C |
7.6 |
7.9 |
8.2 |
Coefficient of thermal conductivity |
20° C |
W/m °K |
16 |
30.0 |
30.4 |
Thermal Shock Resistance |
Tc |
°C |
250 |
200 |
200 |
Dielectricity constant |
1MHz.25℃ |
9 |
9.7 |
9.7 |
|
Dielectric strength |
ac-kV/mm (ac V/mil) |
8.3 (210) |
8.7 (220) |
8.7 (220) |
|
Volume Resistivity |
100℃ |
|