Specifications

1)20 years professional manufacture
2) 18-99% activated alumina
3)Ontime delivery
4)One-stop service
5)ISO9001

 

Description

 

Activated alumina is manufactured from aluminium hydroxide by dehydroxylating it in a way that produces a highly porous material; this material can have a surface area significantly over 200 square metres/g. The compound is used as a desiccant (to keep things dry by absorbing water from the air) and as a filter of fluoride, arsenic and selenium in drinking water. It is made of aluminium oxide (alumina; Al₂O₃), the same chemical substance as sapphire and ruby (but without the impurities that give those gems their color). It has a very high surface-area-to-weight ratio, due to the many "tunnel like" pores that it has

  

Application:

 

 

Activated alumina has much micro paths, so the specific surface is large. It can be used as absorbent desiccant and catalyst carrier. It is also a kind of trace water desiccant and the pole-molecular absorbent, according to the absorbed molecular polarization, the attachment  force is strong for water, oxide, acetic acid, alkali etc.

 

Used as Catalyst ,Desiccant ,Fluoride adsorbent

 

 

Used as a desiccant, it works by a process called adsorption. The water in the air actually sticks to the alumina itself in between the tiny passages as the air passes through them. The water molecules become trapped so that the air is dried out as it passes through the filter. This process is reversible. If the alumina desiccant is heated to ~200°C, it will release the trapped water. This process is called regenerating the desiccant.

 

Activated alumina is also widely used to remove fluoride from drinking water.  

Vacuum systems

In high vacuum applications, activated alumina is used as a charge material in fore-line traps to prevent oil generated by rotary vane pumps from back streaming into the system.

 

Biomaterial

Its mechanical properties and non-reactivity in the biological environment allow it to be a suitable material used to cover surfaces in friction in body prostheses (e.g. hip or shoulder prostheses).

 

 Technical data

 

 

Type Item		Activated alumina absorbent			Activated alumina desiccant			Activated alumina catalyst carrier
		General type	High strength type		General type		Air separation type
Crystal type		Y			X-P			Y
Chemical composition%	AL2O3	≥92	≥93		≥90			≥95
	Na2O	≤0.3
	Other	6-8			<10			<5
Physical property	Size  mm	ø2-3	ø5-8		ø2-3			ø2-3
		ø3-5			ø3-5			ø3-5
		ø4-6			ø4-6			ø4-6
	Surface area m2/g	≥300	300-325		≥300		350±20	200-400
	Porosity ml/g	≥0.35	≥0.5		0.4±0.05		0.4±0.03	0.4-0.6
	Static water absorption %	≥15	17-19		≥15		≥19	≥28
	Bulk density g/ml	0.68-0.72	0.74-0.77		0.68-0.72
	Abrasion rate %	≤0.4
	Crush strength N/granule	ø2-3	≥70	222----311	ø2-3	≥70		ø2-3	≥70
		ø3-5	≥100		ø3-5	≥100		ø3-5	≥100
		ø4-6	≥100		ø4-6	≥100		ø4-6	≥100

 

activated alumina balls , desiccant 18-99% activated alumina

 

 

 

 

 

 

 

Welcome to inquiry!