_ Excellent adhesion to pipe and self

_ Flexibility provides extra protection at vulnerable areas

_ Excellent conformability and consistent uniform thickness

_ Easily applied with no special equipment

_ Compatible with common pipe coatings

_ Excellent resistance to cathodic disbonding

-Resistant to UV

_ Can be applied over a wide temperature range 

_ Good conformability and consistent uniform thickness

_ Cold applied

_ Heavy duty butyl bitumen compound adhesive ensures a strong bond & impervious seal.

PROPERPTIES

UNIT

TEST METHOD

TYPICAL VALUES

 934-40

 934-50

 934-60

 934-65

Total thickness

mil

ASTM D 1000

40mils

50mils

60mils

65mils

Tensile Strength

lb/in

ASTM D 1000

30(5kg/cm)

35(6.3kg/cm)

39(7kg/cm)

42(7.5kg/cm)

Elongation 

%

ASTM D 1000

400

400

450

500

Length

25mtrs

20mtrs

15mtrs

10mtrs

Width

2”,4”,6”,9”

Peel adhesion

  To primed pipe

oz/in

ASTM D 1000

269(3kg/cm)

296(3.3kg/cm)

314 (3.5kg/cm)

340(3.8kg/cm)

     To backing

oz/in

ASTM D 1000

90(1kg/cm)

90(1kg/cm)

117(1.3kg/cm)

135(1.5kg/cm)

Dielectric Strength

KV/mm

ASTM D 1000

42

42.6

43

43.8

Volume Resistivity

ohm·m

ASTM D 257

2.5 X 1012

2.5 X 1012

2.5 X 1012

2.5 X 1012

Water Vapor Transmission Rate 

g/ m2 /24h

ASTM E 96

0.06

0.05

0.03

0.02

Water Absorptivity

%

ASTM D 570

0.1

0.1

0.1

0.1

Application Temperature

°F

-31-+160  (-35-+70°C)

Max service temperature

°F

-40-+176  (-40-+80°C)

Performance

AWWA C-209,ASTM D 1000,EN 12068