HM-180 Primer

Used in priming the base subsrate

HM-180CE Leveling Adhesive

Used in leveling of the base

HM-180C3P Fabric Impregnator/ Adhesive

Used in impregnating the carbon fabric and   pasting it to the substrate

Appearance

Component A: transparent viscous liquid

Operable time (min)

>30

Component B: brown viscous liquid

Finger touch dry time(20 °C,h)

1-2

Bonding strength       

C60 concrete damage

Mixture ratio

2:1

Appearance

Component A: viscous paste

Operable time (min)

>40

Component B: viscous paste

Operating temperature (°C)

5-40

Steel – steel bonding strength (MPa)

shear

  20

Finger touch dry time(20 °C,h)

1-2

tensile

  35

Mixture ratio

2:1

Appearance

Component A: viscous liquid

Operable time (min)

>30

Component B: viscous liquid

Operating temperature (°C)

5-40

Finger touch dry time(20 °C,h)

1-2

Basic properties after pasted carbon fiber cure

Standard value of tensile strength (MPa)

≥40

Ultimate elongation (%)

≥1.5

Elastic modulus (MPa)

≥2500

Mixture ratio

2:1