Product Details

Specifications

1)ISO9001 SGS certificate
2)high quality
3)low price

Characteristic

fast crystallization, easy to mold.

melting temperature reaches to 225oC, high deflection temperature.

fiber glass re-enforced, good mechanical strength

low water absorption rate, low shrinkage rate

resistant to chemical, solvent and natural weather

low warpage

can reach UL94V-0 flammability

ultrasound welding capability

Good electrical resistance

Fire retardant being used in CCP PBT does not contain PBDE & PBB Brominated ingredient.

Application:

· PBT Fiber

· Optical Cable Coatings

· PBT film

· PBT Master Batch

· Glass-Fiber Reinforced & Flame Retardant Grade PBT Compound

· Electronic Parts, Electrical Parts, and Auto Parts

PBT	GF	30G3	15	HB	High rigidity, Heat resistance, Dimension stability
		30G4	20	HB
		30G6	30	HB
	FR	3010F	0	V0	Flame retardance, High flowability
	FR	3010FW	0	V0	Flame retardance, High flowability, Paper white
	FR&GF	30G3F	15	V0	Glassfiber reinforced, Flame retardance, High rigidity, Heat resistance
		30G4F	20	V0
		30G6F	30	V0
	WR	30T1WR	5	HB	Wear resisatnce

PBT MODEL: L08XM L10XM
Property	Test Method	Unite	Value
			L08XM	L10XM
Specific Gravity	ASTM D-792	g/cm3	1.30-1.32	1.30-1.32
Interinsic Viscosiy	Q/SHYH08.4411	Dl/g	0.86+/-0.02	1.035+/-0.02
Melting Point	Q/SHYH08.3026	0C	225min	225min
Carboxyl End Groups	Q/SHYH08.4412	Mol/t	30max	30max
Color L	Q/SHYH08.4413	---	88min	88min
Color B	Q/SHYH08.4413	---	6max	6max
Tensile Strength	ASTM D-638	Mpa	50-60	50-60
Tensile Elongation	ASTM D-638		100min	200min
Dielectric Strength	ASTM D-149	Kv/mm	20min	20min
Nielectric Charpy Impact Strength	ASTM D-256	J/m	40min	40min

Property	Test Criteria	Unit	Fiber Reinforced PBT		ResistanceBurning PBT	Reinforced &Antiburning PBT			Filled PBT	Filled & ResistantBurning PBT
Property	Test Criteria	Unit	101- G20	A01- G30	201T	301- G10	301-G20	301- G30	401- M35	501- M30
Fiber Content	ISO1170	%	18-22	28-30		8-12	18-22	28-32
Density	D-702	G/cm3	1.42	1.53	1.35	1.38	1.46	1.54	1.50	1.78
Molding Shinkage	D-955	%	0.3- 1.0	0.2 -0.9	1.0- 1.3	0.3- 0.7	0.2- 0.9	0.2- 0.7	0.3- 0.8	0.3- 0.8
Tensile Strength	D-638	Mpa	116	130	70	95	110	130	102	104
Elongation at break	D-638	%	3.8	2.5	2.0	3.6	2.8	2.3	1.5	1.5