Product Details

ASTM a514 black steel sheet

ASTM a514 grade c steel sheet

A very popular grade used extensively within the construction industry in earth moving equipment, building / support apparatus, truck frames / bodies, oil rigs, booms, and drilling equipment just to name a few. This quenched and tempered HSLA (High Strength Low Alloy) product have both tensile / yield properties at min 100ksi.

Chemical Requirements

Elements	Grade A, %	Grade B, %	Grade C, %	Grade E, %	Grade F, %	Grade H, %	Grade J, %
Elements	1-1/4 (32)	1-1/4 (32)	1-1/4 (32)	6 (150)	2-1/2 (65)	2 (50)	1-1/4 (32)
Carbon	0.15-0.21	0.12-0.21	0.10-0.20	0.12-0.20	0.10-0.20	0.12-0.21	0.12-0.21
Manganese	0.80-1.10	0.70-1.00	1.10-1.50	0.40-0.70	0.60-1.00	0.95-1.30	0.45-0.70
Phosphorus, max	0.035	0.035	0.035	0.035	0.035	0.035	0.035
Sulfur, max	0.04	0.04	0.04	0.04	0.04	0.04	0.04
Silicon	0.40-0.80	0.20-0.35	0.15-0.30	0.20-0.40	0.15-0.35	0.20-0.35	0.20-0.35
Nickel	-	-	-	-	0.70-1.00	0.30-0.70	-
Chromium	0.50-0.80	0.40-0.65	-	1.40-2.00	0.40-0.65	0.40-0.65	-
Molybdenum	0.18-0.28	0.15-0.25	0.15-0.30	0.40-0.60	0.40-0.60	0.20-0.30	0.50-0.65
Vanadium	-	0.03-0.08	-	^A	0.03-0.08	0.03-0.08	-
Titanium	-	0.01-0.03	-	0.01-0.10	-	-	-
Zirconium	0.05-0.15^B	-	-	-	-	-	-
Copper	-	-	-	-	0.15-0.50	-	-
Boron	0.0025 max	0.0005-0.005	0.001-0.005	0.001-0.005	0.0005-0.006	0.0005-0.005	0.001-0.005
Columbium, max	-	-	-	-	-	-	-


Elements	Grade M, %	Grade P, %	Grade Q, %	Grade R, %	Grade S, %	Grade T, %
Elements	2 (50)	6 (150)	6 (150)	2-1/2 (65)	2 (50)	2 (50)
Carbon	0.12-0.21	0.12-0.21	0.14-0.21	0.15-0.20	0.10-0.20	0.08-0.14
Manganese	0.45-0.70	0.45-0.70	0.95-1.30	0.85-1.15	1.10-1.50	1.20-1.8
Phosphorus, max	0.035	0.035	0.035	0.035	0.035	0.035
Sulfur, max	0.04	0.04	0.04	0.04	0.04	0.01
Silicon	0.20-0.35	0.20-0.35	0.15-0.35	0.20-0.35	0.15-0.35	0.40-0.60
Nickel	1.20-1.50	1.20-1.50	1.20-1.50	0.90-1.10	-	-
Chromium	-	0.85-1.20	1.00-1.50	0.35-0.65	-	-
Molybdenum	0.45-0.60	0.45-0.60	0.40-0.60	0.15-0.25	0.10-0.35	0.45-0.60
Vanadium	-	-	0.03-0.08	0.03-0.08	-	0.03-0.08
Titanium	-	-	-	-	^c	-
Zirconium	-	-	-	-	-	-
Copper	-	-	-	-	-	-
Boron	0.001-0.005	0.001-0.005	-	-	0.001-0.005	0.001-0.005
Columbium, max	-	-	-	-	0.06	-

1)May be substituted for part or all titanium content on a one for one basis.

2)Zirconium may be replaced by cerium. When cerium is added, the cerium/sulfur ratio should be approximately 1.5 to 1, based upon heat analysis.

3)Titanium may be present in levels up to 0.06% to protect the boron additions.

Tensile & Hardness Requirements
NOTE 1 - On plates wider than 24 in. (600 mm), the test specimen shall be taken in the transverse direction. (See Section 10 and Specification A 6/A 6M)

NOTE 2 - Either the full thickness rectangular specimen shown in Fig. 3 of the Methods and Definitions A 370, or the 1/2-in. (12.5-mm) diameter specimen shown in Fig. 4 of Methods and Definitions A 370 may be used for plates over 3/4 to 1-1/2 in. (20 to 40 mm) in thickness.

Thickness, in. (mm)	Ultimate Tensile Strength ksi (MPa)	Yield Strength^Amin, ksi (MPa)	Elongation in 2 in. (50 mm), ^B,C,D,E	Reduction of Area,^B,C	Brinell Hardness^FNumber
To 3/4 (20), incl	110 to 130 (760 to 895)	100 (690)	18	40^G	235 to 293
Over 3/4 to 2-1/2 (20 to 65), incl	110 to 130 (760 to 895)	100 (690)	18	40^G, 50^H	-
Over 2-1/2 to 6 (65 to 150), incl	100 to 130 (690 to 895)	90 (620)	16	50^H	-

1)Measured at 0.2% offset or 0.5% extension under load as described in the Determination of Tensile Properties section of Methods and Definitions A 370.

2)Elongation and reduction of area not required to be determined for floor plates.

3)For plates tested in the transverse direction, the elongation minimum percent is reduced by 2% and the reduction of area minimum requirement is reduced by 5%.

4)When measured on the Fig. 3 (Methods and Definitions a 370) 1-1/2 in. (40mm) wide specimen (see Note 2 of this table), the elongation is determined in a 2 in. (50-mm) gage length which includes the fracture and shows the greatest elongation.

5)For nominal thickness under 5/16 in. (8 mm), a deduction from the specified percentage of elongation shall be made for decreases of the nominal thickness below 5/16 in (8 mm). See elongation requirement adjustments under the Tension Tests section of Specification A 6/A 6M, for deduction values. However, the deduction may not exceed 3%.

6)See Section 8 of this specification.

7)When measured on the Fig. 3 (Methods and Definitions A 370) 1-1/2 in.(40mm) wide, specimen (see Note 2 of this table).

8)When measured on the Fig. 4 (Methods and Definitions A 370) 1-1/2 in.(12.5mm) round specimen (see Note 2 of this table).