Product Details

»Specifications

1.Casting Iron,Casting Steel,Tungsten Carbide
2.Machine Center,CMM
3.Factory Price
4.OEM Service

»Business ability and scope

Material:Ductile casting iron,gray cast iron,stainless steel,carbon steel,low alloy steel,high alloy steel,

hardfacing tungsten carbide, Composite Ceramics etc.

Process:clay sand casting,furan resin sand casting,shell mold casting,water glass sand casting,lost foam casting(EPC or LFC)

Application:Eirich mixer wear parts,Teka mixer wear parts,Sicoma mixer wear parts,Liebherr mixer wear parts etc.

Blades, scrapers ,arm guards and wear liners are the most frequently replaced parts of a mixer. Our casting steel,hard-faced tungsten carbide wear parts will help reduce the amount of time (money) you spend on your mixer.» Materials:

1.1 Hi-chrome

Mechanical Properties
HRC	AK(J/cm ²)	Micro structure	Flexural strength
58-64	≥2.5	M+C	>700 ak N.M/CM2

Chemical Composition (%)
C	Si	Mn	Cr	P	S	Mo	Cu	Ni
1.7-3.2	0.3-1.2	0.3-1.0	10-11	≤0.10	≤0.10	Micro-	Micro-	Micro-

1.2 high manganese steel

Mechanical Properties
Hardness(HB)	Elongation δ (%)	Flexural strength σb (MPa)	Heat treatment criterion
≤229	≥20	≥637	quenching,1060~1100°C,water-cooling

Chemical Composition (%)
C	Si	Mn	S	P
1.10~1.50	0.30~1.00	11.00~14.00	≤0.050	≤0.090

1.3 Cr12MoV

Chemical Composition (%)

1.45~1.70

≤0.40

≤0.030

11.00~12.50

≤0.25

Allowable residuals

≤0.30

0.15~0.30

0.40~0.60

Mechanical Properties
Hardness(HB)	Indentation Diameter(mm)	Heat treatment Criterion
annealing,255~207	3.8~4.2	quenching,≥60HRC

1.4 Tungsten Carbide(WC)

Mechanical Properties
Micro-hardness(MPa)	Elasticity Modulus(GPa)	Compressive Strength(MP)	Coefficient of thermal expansion
17800	71.0	56	3.84×10-6/℃

Main Composition (%)		Impurity Content(%)
W	Total C	Free C	Residual Slag of Chlorination	Fe	Cr	V	TiTaNb	CoNiMo etc.
95-96	3.9 ±0.1	≤0.08	≤0.1	≤0.5	≤0.2	≤0.2	≤0.2	≤0.3