APP bitumen waterproof material

1.Introduction

APP (Atactic Polypropylene) modified bitumen membrane is made by saturating the base in bitumen, or thermoplastic elastomer (such as SBS, APP, APAO, APO), reinforced with polyester or fiberglass, finishing the upward face with polythene membrane, fine sands or mineral slates (or grains) or etc.

2.Specification

Thickness	3mm, 4mm, 5mm
Width	1m
length	10m, 15m, 20m or on demand
Base	Polyester or Fiberglass felt
Surface	PE film, Aluminum foil, Yellow sand, Shale gravel(Schist), colored sand
Type	could self-adhesive
Notice	APP modified bitumen membrane is more suitable for hot district with high temperature. Could be self-adhesive modified bitumen membrane

3. Applications

1) Roof and underground in industrial and civil buildings.

2) Bridge, subway, tunnel, swimming pool, etc.

3) Waste landfill, sewage plant, irrigation system, etc.

4.Advantages

1) The SBS modified bitumen is showed good performance on waterproofness;

2) It will be a high-strength membrane to resist water;

3) Puncture-resisting, tear-resisting, corrosion-resisting, mould-resisting and weather-resisting;

4) Good tensile strength and elongation;

5) Strong adaptability for substrate shrinkage, deformation and cracks;

6) Both high and low temperature resistance, especially in cold areas;

7) Convenient to apply: use heat fusion method in all seasons.

5.Pictures for your reference

Our Factory Show

Certification Show

6. Technical Index(Executive standard: GB18242-2008)

APP Waterproof Membrane Reinforced base		PY			G
Type		I	II		I	II
Content of soluble substances(g/m2)≥	2mm				1300
	3mm	2100
	4mm	2900
Water impermeability	Pressure (Map)	0.3		0.2		0.3
	Retention time (min)	Impermeability within 30 min
Heat resistance °C		110	130		110	130
Tensile strengthN/50mm≥	Longitudinal	450	800		350	500
	Transverse				250	500
Elongation at break %≥	Longitudinal	25%	40%		-------	-------
	Transverse
Tear strength N≥	Longitudinal	250	350		250	350
	Transverse				170	200
Low temperature flexibility°C		3	-10		3	-10

7.Storage and Transportation

1) Different type and specification should be stacked separately;

2) Avoid sun-scorched and rain-drenched, Be ventilation;

3) The storage temperature should below 50°C;

4) It have to be one storey when keep in storage stand on end, and shouldn't be more than two storeys when transporting;

5) Avoid tilting or lateral drift, Covered with tarpaulin if need;

6) Base on the normal storage and transportation, the storage period is one year from the date of production.

8. Construction Technology

1) Base processing: the base surface must be clean, solid, level, dry; no grit, rift and loosing dust. For a large recess, fill it with cement mortar and then level it. Remove the protrusion and clean dust. If working on base slab or lateral face, water lowering should be done.

2) Painting primer: before laying the membrane, clean the dust on the surface of concrete base with dust catcher or dust-blower.

3) Heat to melt: place membrane correctly, fire torch, heat the membrane with base entirely, when the surface of the membrane is black and bright with a fusion layer, apply the membrane and press it into a solid and flat state. Before the membrane is cool, seal the edge of joint by float.

4) Requirements for lapping: There should be less than 3 layers of lapping, with the joint seams appearing as "T" type, avoid 4 layers of lapping. The width of longitudinal lapping is between 50 and 80mm, and of end-lap joint 100mm.

Sample is free of charge.

Reasonable Price, Excellent Quality & Attentive Service

The delivery time is about 15-20 days after receiving the deposit.

We offer not just excellent products but service and market solutions.

Welcome to visit our homepage or contact with us for more information.