Specifications

hotmelt glue stick
1.two-part paste
2.repair worn parts, castings, defects
3.250g/pairs

   

   Kafuter K-9113 aluminum hotmelt glue stick epoxy putty  

Typical Properties:

 

Model	Color	Density	Compressive strength	Tensile strength	Shear strength	Bending Strength	Hardness(shore A)	Working Temp.
K-9113	yellow	1.62 g/cm3	92.6 Mpa	36.5 Mpa	24.2 Mpa	51.5 Mpa	88 Mpa	-60~170°C

 

 

 Applications:

  

Two parts, gel formulation, use aluminite powder as filler, the color is consistent with aluminum castings, mainly apply in rebuilding the worn parts, filling the cracking, and impairing the defects in aluminum castings.

 

Directions:

 

1.Surface Cleaning:

 Remove the oil and grease from the surface, also should be abrasived and polished.

 

2. Mixing

 Two-part, please mix and forge the two parts by equal ratio. It will become gel-formulation at the low temperature, it can change into soft gel heating by the heating producer.

 

 Notice: Do not heat with the open-fire

After 24h room cure, it can put into use.

 

3.Coating

 First, coating the surfaces with some glue, and then push and repeat coating the surface until it exhaust the air and fully fill the gap. 

 

4.Curing

 When the room temperature is lower than 10°C, and after 1-2 h room cure, use heat producer heating for 3-4 hour bewteen 80°C, the heating producer between the parts should keep a distance of 300-400mm. and the small-area fittings can be put into the oven for heating below 80°C.

 (Heat Producer: infra-red lamp, electric stove, and other heating sources, not use the open-fire)

 

 5.Post-Processing

 After cured some time, it can be processed by ordinary ways, and wait for 18 hour, it can use the machine for processing.

 

Packing:250g/pairs