Product Details

Specifications

aluminium composite panel with PE or PVDF coated, different colour and size is available

Aluminium composte panel/Nano Aluminium composite panel

Introduction

Nano ACPs adopt unique PVDF of metal construction paint and Nanometer additive, activates with tetrafluoroethylene polymer with long-chain acrylic, and goes into the deep coating. Through the advanced technology of coating processing, the product could keep the Nanometer article long-term stability. And this invention solves Nanometer article not durable and easy dropping shortcomings of the Nanometer technology. Thus the organic Nanometer coating of dirty resistance, self-cleaning comes into a practical moment.

Specification

Panel Thickness(mm)	2mm-8mm
Aluminium Skin Thickness(mm)	0.08mm-0.5mm
Width(mm)	1220mm-2000mm
Length(mm)	2440mm-8000mm

Features

-Excellent easy-cleaning

-Pollution resistance

-Oil resistance

-Good Friction Resistance

-Strong Acid & Alkali Resistance

-Outstanding weather resistance

Applications

-Constructional exterior curtain walls;

-Decorative renovation for storey-added old buildings;

-Indoors decoration for interior walls, ceilings, bathrooms, kitchens and balconies;

-Advertisement board, display platforms and signboards;

-Wallboard and ceilings for tunnels;

-Raw materials in industrial purpose;

-Materials used for vehicle and boat.

SGS Test For 4mm PVDF A.C.P

Items	Standard	Results
Appearance	Clean surface without swell,flaws.scrath and aberration	pass
	Length: ± 3mm	0mm~+2mm
	Width: ± 2mm	0mm~+1mm
	Thickness: 0. 2mm	0mm~+0.14mm
Deviation of dimension	Deviation of diagonal: ≤ 5mm	1mm
	Out of straight at sides: ≤ 1mm/m	0.2mm/m
	Warp: ≤ 5mm/m	1mm/m
Thickness of coating	≥ 25um	29u (av.30)
Deviation of luster	≤ 10	2.1 (av.28.0)
Hardness of pencil	≥ HB	3H
Toughness of coating	≤ 2T	2T
Adhesive	Not less than Grade1	Squaring off method of Grade 0 Grade 1marking method of rolling line
Impact strength	50Kg.cm Without paint off and crack	Pass
Boiling water resistance	(Boiling for 2h without change)	Unchanged
Acid resistance	Immerse surface with5%HCI(v/v)for 48h without change	Unchanged
Alkali resistance	Immerse surface with5%NaOH(m/m)for 48h without change	Unchanged
Oil resistance	Immerse surface with 20# engine oil for 48h without change	Unchanged
Solvent resistance	Clean 100 times with butanone without change	Bottom unrevealed
Cleaning resistance	≥ 10000 times without change	Unchanged
Abrasion resistance	≥ 5L/um	5.33L/um
Contamination resistance	≤ 15%	0.078
Density of surface	Specified value: ± 0.5Kg/m2	5.32Kg/m2
Bend strength	≥ 100Mpa	121Mpa
Flexuous modulus of elasticity	≥ 2.0×10 4 Mpa	3.12 × 104 Mpa
Through resistance	≥ 9.0kN	9.94kN
Cutting strenght	≥ 28.0Mpa	32.0Mpa
180 o peel strength	≥ 7.0N/mm	11.2N/mm
Resistance to change of temperature	-40 ⁰C~80⁰C 20 cycles without change	Unchanged
Heat deformation temperature	≥ 95⁰C	120⁰C
Coefficient of heat expansion	≤ 4.00×10 -5⁰C -1	1.98 × 10 -5⁰C -1
Salt haze resistance (3000h)	Not less than Grade2	Grade 1
Artificial resistance aberration(200h)	≤ 3.0	1.24
Aging resistance Out of light(200h)	Not less than Grade2	Grade 1
other aging characteristic(200h)	Grade 0	Grade 0