Specifications

1. materials:borosilicate 3.3
2. temperature:260c
3. Three reflex, four grooves
4. Very clear, No bend
5. Acid-resistant

Alias: 

   Also named Sight Glass,Reflex Glasses,Level Gauge Glass,Spares for level gauge,

   Boiled Gauge Glass,Boiled Parts,ect

Material:

   Its made from Borosilicate

Usage:

   it is used in lever gauge in boiler for water position.

 Category:

    1) Three tendons (four grooves)

    2) Two tendons (three grooves)

  Level Gauge Glass Physical Property:

    1. Appearance

     1) Air bubble:

          Diameter≤0.5mm, in the 10mm x 10mm area the quantity must be ≤3.Diameter from

       0.5mm to 1.5mm dispersive air bubble, there is less 2 on the sight plane and less 5

       on the No-sight plane. Their distance must be 40mm.

       The air bubble of Diameter from 1.5mm to 2mm ≤3 on the No-sight plane. Their distance

       must  40mm.

       On the sight plane, The distance to the side in 7.5mm,the air bubble of the diameter1mm

       mustnt be more 2mm.

    2) The glass dont allow slag and scrap iron, etc. impurity. 

    3) Stripe: dont allow have palpable filaceous and pectinate stripe on the sight plane.

    4) Cockle: In the side face, dont allow have the cockle of depth1mm.

    5) Crack: dont allow have crack.

    6) Scrape: On the sight plane and in the 7.5mm to edge, the scrape of less than 10mm

       dont allow more 2 strips.

   7)The sight plane must be polishing, and sealing side must be rubbing and polishing.

   2. Color and Lustre

         It should be no color and transparent,and with its self tine green is allowed.

    3. Water-resistance

       Cooked in the water for 5 hours, then weigh up, then titration with 25ml 0~31ug/g

    4. Alkali-resistance

       Cooked in the 0.5N NaOH for 3 hours,then Weigh up,weightlessness should be ≤75mg/dm2

    5. Temperature-resistance impacts capability

        Put it into electric cooker, keep for 7min under the temperature of 260±1, then, put into

       the water of 20±1,it should not crack

    6. Bend-resistance≥80MPa