Specifications

DJD-103

Products Introduction

DJD-103 blend polyols use cyclopentane as blowing agent, which applies to refrigerators, freezers, and other insulation products. The characteristics of the products are as follows: 1.excellent flowability, the density of the foam is well-distributed, and the thermal conductivity is low;

2.excellent low-temperature dimensional stability and good cohesiveness;

3. demould time is 6-8 minutes.

Physical Properties

Appearance                                  pale yellow transparent viscous liquid

Hydroxyl Value mgKOH/g                                   360-420 

Dynamic Viscosity (25 °C) mPa.s                  3000-4000

Gravity (20 °C ) g/ml                                            1.06-1.08

Storage Temperature °C                                      10-25

Storage Stability month                                             6

Recommended Ratio                           pbw 
DJD-103 blend polyols                                  100

CP  or CP/IP                                                   12-14

Isocyanate                                                    136-142

Technology and Reactivity  (the exact value varied depending on processing conditions)

                                                                  Manual Mixing          Mechanical Foaming 

Raw material Temperature °C                 20-25                             20-25

Mold Temperature °C                                 35-40                             35-40 

CT s                                                               12-16                              8-12

GT s                                                               75-85                             50-70

TFT s                                                           100-120                         70-100

Free Density kg/m3                                     25-26                             24-25

Foam Performance

Foam Density by Molding                                 GB/T 6343            35kg/m3

Closed-cell Rate                                                GB/T 10799         ≥90%   

Thermal Conductivity (15 °C)                           GB/T 3399            ≤22 mW/(m.K)

Compressive strength                                                                

(perpendicular to the direction of rising)       GB/T 8813            ≥150kPa

Dimensional Stability    (24h, -20 °C)            GB/T 8811            ≤0.5% 

                                           (24h, 100 °C)                                           ≤1.0% 