Brass is a binary alloy composed of copper and zinc that has been produced for millennia and is valued for its workability, hardness, corrosion resistance and attractive appearance.
Three different types of crystal structure can form as a result of these factors:
1. Alpha Brasses: Alpha brasses contain less than 37% zinc melted into copper and are named for their formation of a homogenous (alpha) crystal structure. Such brasses are softer than their counterparts and, therefore, more easily cold worked, welded and brazed.
2. Alpha-Beta Brasses: Alpha-beta brasses contain between 37-45% zinc and are made-up of both the alpha grain structure, as well as a beta grain structure that is more similar to that of pure zinc. More common than alpha brass, alpha-beta brass is both harder and stronger and, consequently, is usually hot worked by extrusion or stamping and die-casting.
3. Beta Brasses: Although much more rarely used than alpha or alpha-beta brasses, beta brasses make-up a third group of the alloy that contain greater than 45% zinc content. Such brasses form a beta structure crystal and are harder and stronger than both alpha and alpha-beta brasses. As such, they can only be hot worked or cast.
H96 | CuZn5 | 2.0220 | CuZn5 | CE500L | CuZn5 | C21000 | C2100 |
H90 | CuZn10 | 2.0230 | CuZn10 | CW501L | CuZn10 | C22000 | C2200 |
H85 | CuZn15 | 2.0240 | CuZn15 | CW502L | CuZn15 | C23000 | C2300 |
H80 | CuZn20 | 2.0250 | CuZn20 | CW503L | CuZn20 | C24000 | C2400 |
H70 | CuZn30 | 2.0265 | CuZn30 | CW505L | CuZn30 | C26000 | C2600 |
H68 | CuZn33 | 2.0280 | CuZn33 | CW506L | CuZn35 | C26800 | C2680 |
H65 | CuZn36 | 2.0335 | CuZn36 | CW507L | CuZn35 | C27000 | C2700 |
H63 | CuZn37 | 2.0321 | CuZn37 | CW508L | CuZn37 | C27200 | C2720 |