Product Details

Specifications

1.Polished surface,free of oil
2.Good workability and drawability
3.Anti-corrosion
4.Excellent electric conductivity

(Temper)	A(TB00)	H(TD04)	AT(TF00)	HT(TH04)
(Tensile Strength)ksi/Mpa	60-85/410-590	90-125/620-860	165-200/1140-1380	180-220/1240-1520
0.2% Yield Strength) ksi min/Mpa min	20/140	75/520	145/1000	155/1070
(Elongation in 4D% min)	20	8	4	2
(Hardness) HR/HV	B45-85/159-168	B88-102/175-330	C36-42/315-390	C38-44/350-410
(Electrical Conductivity %IACS min)	17	15	22	22
(Typical Age Hardening)			315-320℃×1.5-2hrs	315-320℃×1-2hrs

Beryllium copper (BeCu), also known as copper beryllium (CuBe),

Alloy 25 beryllium copper (C17200 & C17300) is an age-hardening alloy which attains the highest strength of any copper base alloy. It may be age hardened after forming into springs, intricate forms or complex shapes. It has superb spring properties, corrosion resistance and stability as well as good conductivity and low creep.

Tempered beryllium copper is Alloy 25 (C17200 & C17300) that has been age hardened and cold drawn. No further heat treatment is necessary except for a possible light stress relief. It is sufficiently ductile to wind on its own diameter and can be formed into springs and most shapes. Tempered wire is most useful where the properties of beryllium copper are desired, but age hardening of finished parts is not practical.

Specification

All dimensions are according to customers requirements.

Characteristics and Appliances

Beryllium copper is a ductile, weldable, and machinable alloy. It is resistant to non-oxidizing acids (for example, hydrochloric acid, or carbonic acid), to plastic decomposition products, to abrasive wear and to galling. Furthermore, it can be heat-treated to improve its strength, durability, and electrical conductivity. Beryllium copper attains the highest strength (to 1,400 MPa (200,000 psi)) of any copper-based alloy.

Beryllium copper is a non-ferrous alloy used in springs, spring wire, load cells and other parts that must retain their shapes during periods in which they are subjected to repeated stress and strain. Due to its electrical conductivity, it is used in low-current contacts for batteries and electrical connectors.

Workshop

Manufacture Facility

Warehouse

About shipment

1. By sea, by air, by door to door express (FedEx, UPS, DHL, TNT, EMS).
2. For Air Shipment, Please choose your favorite, shipping method according your detail requirement
3. The shipping discount is different because of different weight and destination, we will choose the cheapest and safest way according to your detailed requirement.
4. Normally, it will take around 3-7days from China to destination country.