Specifications

Used in brazing aluminium and aluminium alloy at the temperature of 450 to 620 in the method of flame brazing & furnace brazing.

 

 

QJ201 is a new kind of aluminium brazing flux matching aluminium base filler metal. It is widely 

used in brazing aluminium and aluminium alloy at the temperature of 450 to 620°C in the method 

of flame brazing, and furnace brazing. It can remove aluminium oxide effectively, and promote 

filler metal flowing and spreading in aluminium alloy. QJ201 is a common aluminium flux.

 

Physical Status: Granularity:≤150μm   Density: 1.3-1.4   Standard: JB/T6045-92

 

Main Compositions: Alkali metal, alkaline-earth metal chlorides, fluoride, and active agent.

 

Operation: In advance, properly place the brazing filler metal on the brazing joint which will be heated 

together with the workpieces. In the process of manual torch brazing, firstly, the brazing wire need to 

be tipped with the flux. Then, after the work pieces are heated to the brazing temperature, the brazing 

wire is manually handled to keep close to the brazing joint. The wires are evenly heated by the outer 

flame from the Multiples holes brazing torch. To protect the metallic materials, the flame should be placed 

at the proper distance away from the wires to avoid the oxidation the work pieces, producing high quality 

brazing seams.

 

Post treatment: 

The residue of the QJ201 aluminium brazing flux attached on the work pieces is corrosive which should

be cleaned timely.