Specifications

It is mainly used for drawing the core of wires and cables
The surface of the rod is clean, smooth and seamless.

9.5mm bare Aluminium Wire Rod

 

 

 

 

Specifications

 

It is mainly used for drawing the core of wires and cables

The surface of the rod is clean, smooth and seamless.

Coil weight: large coil≤1000kg, small coil: 300--1000kg

Aluminum Rod was produced and provided by consulting and following the American standard ASTM B233 and Germany standard EN17152

1.Producing and providing the products according to Chinese standard GB/T3954-2001, and consulting and following the American standard ASTM B233:1997, and Germany DIN standard EN 17152:1997

  aluminium rod

 

2.The Type,Condition and Range

Type	Condition	Range(mm)
A	o	Φ9-20
A2,A4,A6,A8	H/R

  aluminium rod

 

3.The Mechanics and Electric Function

Type	Tensile Strength (M pa)	Percentage Elongation (%≥)	Resistivity at 20°c (nΩ.m≤)
A	60-80	25	27.55
A2	80-100	12	27.85
A4	95-115	10	28.01
A6	110-130	8	28.01
A8	120-150	6	28.01

 

4.The Component of Material

Name of Element	Si	Fe	Cu	V+Ti+Mn+Cr	Other	Al
Percentage %	≤0.11	0.25	0.01	0.02	0.03	≥ 99.61

  aluminium rod

 

5.Standard specification for Aluminum 1350 Drawing Stock for Electrical Purposes

 

TABLE 1- Tensile Property Limits

Temper	Tensile Strength
	Ks j	M pa
1350-O	8.5-14.0	59-97
1350-H12 and-H22	12.0-17.0	83-117
1350-H14 and-H24	15.0-20.0	103-138
1350-H16 and-H26	17.0-22.0	117-152

 

TABLE 2- Electrical Resistivity Limits

Temper	Resistivity	Equivalent Volume Conductivity,%
	Max.Ω.mm2/m	IACS Min.
1350-O	0.027899	61.8
1350-H12 and-H22	0.028035	61.5
1350-H14 and-H24	0.028080	61.4
1350-H1 aluminium rod 6 and-H26	0.028126	61.3

 

 